IROGRAN® CA116-205
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Huntsman Corporation |
| Trademark: | IROGRAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tIKhGG_IROGRAN-CA116-205.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
IROGRAN CA116-205 is a high performance polyester based thermoplastic polyurethane intended for flat die extrusion applications. IROGRAN CA116-205 is part of the HUNTSMAN film and sheet product range and offers a specially designed, flexible plasticizer free product suitable for the preparation of extruded films with enhanced adhesion following lamination. PERFORMANCE FEATURES
APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.15 | g/cm³ | ASTM D792, DIN 53478 |
| Melt Volume-Flow Rate (MVR) (190°C/5.0 kg) | 60.0 | cm³/10min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, Injection Molded) | 95 | ASTM D2240, DIN 53505 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 2 | |||
| 100% Strain, 0.635 mm | 5.45 | MPa | ASTM D412 |
| 100% Strain, 0.635 mm | 3.00 | MPa | DIN 53504 |
| 300% Strain, 0.635 mm | 6.27 | MPa | ASTM D412 |
| 300% Strain, 0.635 mm | 4.00 | MPa | DIN 53504 |
| Tensile Strength 3 | |||
| Break, 0.635 mm | 10.0 | MPa | ASTM D412 |
| Break, 0.635 mm | 17.2 | MPa | DIN 53504 |
| Tensile Elongation 4 | |||
| Break, 0.635 mm | 650 | % | ASTM D412 |
| Break, 0.635 mm | 600 | % | DIN 53504 |
| Tear Strength 5 | |||
| 0.635 mm | 80.6 | kN/m | ASTM D624 |
| 0.635 mm | 110 | kN/m | DIN 53515 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 80.0 to 110 | °C | Internal Method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 40.0 | °C | |
| Drying Time | 4.0 | hr | |
| Hopper Temperature | 149 | °C | |
| Cylinder Zone 1 Temp. | 154 | °C | |
| Cylinder Zone 2 Temp. | 154 | °C | |
| Cylinder Zone 3 Temp. | 154 | °C | |
| Cylinder Zone 4 Temp. | 154 | °C | |
| Cylinder Zone 5 Temp. | 154 | °C | |
| Adapter Temperature | 154 | °C | |
| Die Temperature | 154 | °C |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | Extruded Film |
| 3 . | Extruded Film |
| 4 . | Extruded Film |
| 5 . | Extruded Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Michithene R6300 | API Polymers, Inc. | HDPE | Michithene |
| CP PRYME® Polycarbonate PC100RULUV-10M Clear | Chase Plastics Services Inc. | PC | CP PRYME® Polycarbonate |
| Exceed™ 0019XC | ExxonMobil Chemical | mPE | Exceed™ |
| Ducor® 2300 K | Ducor Petrochemicals BV | PP Impact Copolymer | Ducor® |
| OTECH TPO OTR2588-Molding | OTECH Corporation | TPE | OTECH TPO |