Infino TH-1100
| Category: | PC , Polycarbonate |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tHVauB_Infino-TH-1100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino TH-1100 is a Polycarbonate (PC) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 17 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955, ISO 2577 | ||
| Flow : 3.20 mm | 0.49 to 0.60 | % | |
| Across Flow : 3.20 mm | 0.51 to 0.62 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2060 | MPa | ASTM D638 |
| -- | 2000 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 63.7 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Break 3 | 68.6 | MPa | ASTM D638 |
| Break | 60.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 100 | % | ASTM D638 |
| Break | 92 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2160 | MPa | ASTM D790 |
| -- 6 | 2400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 94.1 | MPa | ASTM D790 |
| -- 8 | 95.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | > 49 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 130 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 123 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 144 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (2.00 mm) | V-0 | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (3200 µm) | 86.0 | % | ASTM D1003 |
| Haze (3200 µm) | 2.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 110 | °C | |
| Desiccant Dryer | 110 | °C | |
| Drying Time | |||
| -- | 2.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 260 to 270 | °C | |
| Nozzle Temperature | 290 | °C | |
| Mold Temperature | 40.0 to 120 | °C | |
| Injection Pressure | 49.0 to 245 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMIPEX® MM | Sumitomo Chemical Co., Ltd. | Acrylic (PMMA) | SUMIPEX® |
| Moplen EP641P | PolyMirae | PP Copolymer | Moplen |
| TOTAL Polypropylene PPC 1645 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| WPP PP PPH3TF2-Natural | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| Chemlon® 233 GU | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |