Andur M-22 (HQEE)
| Category: | PUR-Ester/MDI , Polyurethane (Polyester, MDI) |
| Manufacturer: | Anderson Development Company |
| Trademark: | Andur |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tGPWm6_Andur-M-22-HQEE-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Andur M-22 is an MDI-Ester prepolymer that, when processed with close attention to handling procedures and formulation, produces high quality elastomers. These elastomers perform very well in dynamic applications. |
| General Information | |
|---|---|
| Forms |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A | 96 | ASTM D2240 | |
| Shaw D | 43 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Strength | ASTM D695 | ||
| 2% strain | 1.17 | MPa | ASTM D695 |
| 5% strain | 2.41 | MPa | ASTM D695 |
| 10% strain | 3.79 | MPa | ASTM D695 |
| 15% strain | 5.17 | MPa | ASTM D695 |
| 20% strain | 6.76 | MPa | ASTM D695 |
| 25% strain | 8.27 | MPa | ASTM D695 |
| Taber Abrasion Resistance | 16.9 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 10.0 | MPa | ASTM D412 |
| 300% strain | 17.2 | MPa | ASTM D412 |
| Tensile Strength (Yield) | 31.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 550 | % | ASTM D412 |
| Compression Set | 35 | % | ASTM D395 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life | 6.0 - 10 | min | |
| Demold Time | 90 | min |
| Additional Information |
|---|
| Die C Tear, ASTM D1004: 765 pliAverage Split Tear, ASTM D1938: 425 pliStoichiometry Curative Level: 90%Break Set, ASTM D412-80: 40%NBS Abrasion: 385% Rubber StandardParts of curative per 100 parts Andur M-22, 6.5% NCO: 13.93 parts by weightParts of curative per 100 parts Andur M-22, 6.55% NCO: 14.04 parts by weightParts of curative per 100 parts Andur M-22, 6.6% NCO: 14.14 parts by weightParts of curative per 100 parts Andur M-22, 6.65% NCO: 14.25 parts by weightParts of curative per 100 parts Andur M-22, 6.7% NCO: 14.36 parts by weightMix Temperature: Andur M-22: 221-230°F Curative HQEE: 230°F Stability: Ambient Temperature, 25°C: 6 Months Melting Temperature, 60°C: 1 Month Processing Temperature, 90°C: 12 Hours Processing Temperature, 105°C: 3 Hours |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 110 - 140 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROMID B 280 Z1 G6 | Taro Plast S.p.A. | Nylon 6 | TAROMID B |
| Viprene™ G40D-32U-BLK | Alliance Polymers & Services | TPV | Viprene™ |
| ULTEM™ CRS5211R resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| Karina CLEAR PVC COMPOUND -E 57/200-D-AT-IS-SI-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 7011EE-75 BLACK | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |