NORYL PPX™ PPX7110 resin
| Category: | PPE+PS+PP , Polyphenylene Ether + PS + PP |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL PPX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tFyQpI_NORYLPPXPPX7110resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPE+PP blend. High Impact, Good Heat Resistance |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.968 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 11 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.80 - 1.2 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1340 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 35.9 | MPa | ASTM D638 |
| Fracture | 32.4 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 6.5 | % | ASTM D638 |
| Fracture | 200 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 1550 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 51.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 150 | J/m | ASTM D256 |
| 23°C | 440 | J/m | ASTM D256 |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Total Energy | 27.8 | J | ASTM D3763 |
| 23°C, Total Energy | 38.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 113 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 77.2 | °C | ASTM D648 |
| Vicat Softening Temperature | 139 | °C | ASTM D1525 6 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 8.1E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 1.1E-4 | cm/cm/°C | ASTM E831 |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI | 50.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.52 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 65.6 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 - 70 | % | |
| Rear Temperature | 227 - 277 | °C | |
| Middle Temperature | 238 - 282 | °C | |
| Front Temperature | 249 - 288 | °C | |
| Nozzle Temperature | 260 - 288 | °C | |
| Processing (Melt) Temp | 260 - 288 | °C | |
| Mold Temperature | 32.2 - 48.9 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Vent Depth | 0.038 - 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 201H UV HS | RTP Company | Nylon 66 | RTP |
| RTP 383 TFE 10 EM | RTP Company | PC | RTP |
| Shandong PA6 A1G6304 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 6 | Shandong PA6 |
| Andur 8 APLM/Curene® 442 | Anderson Development Company | PUR-Ester/TDI | Andur |
| DOWLEX™ 2027G | The Dow Chemical Company | LMDPE | DOWLEX™ |