Lutene® BB0808
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lutene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tFgoRO_Lutene-BB0808.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LUTENE BB0808 is mainly intended for the extrusion of blown film with high mechanical property for the manufacture of shrink film and pallet shrink covers. LUTENE BB0808 have the balanced shrink properties and good clarity make suitable for shrink film. LUTENE BB0808 contains neither slip agent nor antiblock agent. Applications: Shrinkage film, Pallet shrink cover, chopping board, All types of industrial packing. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.921 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (F50) | > 500 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Resistance | ASTM D1922 | ||
| MD | 27.5 | MPa | ASTM D1922 |
| TD | 27.5 | MPa | ASTM D1922 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Nitrogen Permeability | 3500 | cm³/m²/24 hr | Internal method |
| Film Thickness - Tested | 50 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Fracture | 21.6 | MPa | ASTM D882 |
| TD : Fracture | 20.6 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 550 | % | ASTM D882 |
| TD : Fracture | 650 | % | ASTM D882 |
| Dart Drop Impact | 220 | g | ASTM D1709 |
| Oxygen Permeability | 2000 | cm³/m²/24 hr | Internal method |
| Water Vapor Transmission | 12 | g/m²/24 hr | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 94.0 | °C | ASTM D1525 |
| Melting Temperature | 110 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°) | 80 | ASTM D2457 | |
| Haze | 8.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 - 190 | °C |
| Extrusion instructions |
|---|
| Blow up ratio: 1.5 to 3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNO ABS H530L | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| Ultramid® B3EG7 | BASF Corporation | Nylon 6 | Ultramid® |
| ACRYLITE® Sheet Solar 0Z023 | Evonik Cyro LLC | Acrylic (PMMA) | ACRYLITE® Sheet |
| Ecomass® 1080CO94 | Ecomass Technologies | Nylon, Unspecified | Ecomass® |
| VALOX™ SHF4320 resin | SABIC Innovative Plastics Europe | PBT | VALOX™ |