CERTENE™ LDI-4023
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tFgaHT_CERTENE-LDI-4023.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LDI-4023 is a certified prime grade specially designed for High-Flow INJECTION MOLDING applications requiring good balance of mechanical and low warpage properties. LDI-4023 features very good processability over a wide range of molding conditions, good clarity, excellent flexibility, and high surface appearance of molded articles. LDI-4023 applications include housewares, lids, closures, overcaps, medical parts, and general purpose molded articles. Recommended processing temperature is170 to 220°C., with mold at 20 to 40°C.. LDI-4023 complies with FDR regulation 21CFR 177.1520 (c) 2.2 and most international regulations concerning the use of Polyethylene in contact with food articles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 40 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 13.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 50 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 3 | 317 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength | 73.6 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | 0.00 | °C | ASTM D746 |
| Vicat Softening Temperature | 88.0 | °C | ASTM D1525 |
| Additional Information |
|---|
| Test specimens from compression molded plaque according to ASTM D 1928 Procedure C. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 170 - 220 | °C | |
| Mold Temperature | 20.0 - 40.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6000 HWUVCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| Garathane™ X 96-322-A NAT | AlphaGary | PVC Alloy | Garathane™ |
| Genestar™ TA112 | Kuraray Co., Ltd. | Nylon 9T | Genestar™ |
| Plaslube® Actrn | Techmer Engineered Solutions | Acetal (POM) Homopolymer | Plaslube® |
| Softell TKS 209N NAT | LyondellBasell Industries | PP Copolymer | Softell |