POLYFORT® FIPP 30 T K1005
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | A. Schulman Europe |
| Trademark: | POLYFORT® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tFgVvs_POLYFORT-FIPP-30-T-K1005.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% talc filled PP-Copolymer; long term heat stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 6.00 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 62.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 27.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 3.5 | % | ISO 527-2/1A/50 |
| Flexural Modulus | 3250 | MPa | ISO 178 |
| Flexural Stress | 45.0 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength | 4.6 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | ISO 179/1eA |
| 23°C | 7.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 19 | kJ/m² | ISO 179/1eU |
| 23°C | 55 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 110 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 67.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 147 | °C | ISO 306/A50 |
| -- | 66.0 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 1.50 mm | HB | IEC 60695-11-10, -20 | |
| 3.00 mm | HB | IEC 60695-11-10, -20 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP400M | PolyMirae | PP Copolymer | Moplen |
| Formolene® 6335N | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| Geon™ Vinyl Flexible R8570A | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Bergamid™ A700 G15 HW UF NC099 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Hostacom BC 1177 A BLACK | LyondellBasell Industries | PP Copolymer | Hostacom |