Hapweld™ 36

Category:	TP, Unspecified , Thermoplastic
Manufacturer:	Hapco Inc.
Trademark:	Hapweld™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	tF0bL1_Hapweld-36.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

A two part, non-shrinking, 100% solids, amber clear, polymer adhesive which cures at room temperature. It is a flowable polymer adhesive which forms permanent structural bonds between similar and dissimilar materials.

Once hardened, HAPWELD 36 resists moisture, water, solvents, chemicals, and retains good bond strength up to 160°F.

May be used from 2:1 to 1:1 by volume or by weight, making it ideal for both field and production applications.

The "workhorse" of our polymer adhesive line and will bond most metals, plastics, ceramics, wood, fabrics, canvas, etc. As you increase the mix from 2:1 to 1:1, the cured product becomes semi-rigid and has lower heat resistance

General Information
Features	Bondability Good Chemical Resistance Low Shrinkage Moisture Resistant Solvent Resistant
Uses	Adhesives
Appearance	Clear Amber
Forms	Liquid

Physical	Nominal Value	Unit
Weight - Per gallon	4000	g

Thermal	Nominal Value	Unit
Service Temperature	-73 to 71	°C

Thermoset	Nominal Value	Unit
Work Time ¹	0.7 to 2.0	hr

Additional Information	Nominal Value	Unit
Cure Time (21°C)	1.0 to 2.0	day

Hardness	Nominal Value	Unit
Durometer Hardness (Shore D)	80

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength	56.9	MPa
Shear Strength	29.0	MPa	ASTM D732

Electrical	Nominal Value	Unit
Volume Resistivity (25°C)	1.0E+16	ohms·cm
Dielectric Constant (25°C)	3.50

Thermoset	Nominal Value	Unit
Thermoset Components
Part A ²	Mix Ratio by Weight: 1.0, Mix Ratio by Volume: 1.0
Part A ³	Mix Ratio by Weight: 2.0, Mix Ratio by Volume: 2.0
Part B ⁴	Mix Ratio by Weight: 1.0, Mix Ratio by Volume: 1.0
Part B ⁵	Mix Ratio by Weight: 1.0, Mix Ratio by Volume: 1.0
Thermoset Mix Viscosity	30000	cP

Note Message
1 .	Depending on mix ratio. Longest working life is at 2 parts A to 1 part B, and the shortest is at 1:1 mixing ratio.
2 .	Semi-rigid
3 .	Hard
4 .	Semi-rigid
5 .	Hard

Resin Grade	Manufacturer	Category	Trademark
REPOL® AMI035N	Reliance Industries Limited	PP Impact Copolymer	REPOL®
Quadraflex™ ARE-90A	Biomerics, LLC	TPU-Polyether	Quadraflex™
MAXATEL® AH500ALTF5-NC010	Pier One Polymers, Inc.	Acetal (POM) Homopolymer	MAXATEL®
Hostacom HBG H01	LyondellBasell Industries	PP Homopolymer	Hostacom
SECCO GPPS-251	Shanghai SECCO Petrochemical Co., Ltd	PS (GPPS)	SECCO