Moplen RP220M
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tElNeW_Moplen-RP220M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
"Moplen" RP220M is a controlled rheology medium modified propylene random copolymer for manufacturing high transparent cast films. It contains no slip or antiblocking agents. It offers good processability, excellent clarity and gloss and exhibits very good heat weldability. Main applications are packaging of foodstuffs, packaging of stationary, shirts and hosiery. It is also suitable for production of stationary folders. "Moplen" RP220M is suitable for food contact. For regulatory information please refer to "Moplen" RP220M Product Stewardship Bulletin ( PSB ). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 23.0 | MPa | |
| Break | 26.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 12 | % | |
| Break | > 500 | % | |
| Flexural Modulus | 700 | MPa | ISO 178 |
| Coefficient of Friction (Dynamic, Cast Film) | > 1.0 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Secant Modulus | |||
| MD : 50 µm, Cast Film 1 | 560 | MPa | ASTM D882 |
| MD : 50 µm, Cast Film | 500 | MPa | MA 18068 |
| TD : 50 µm, Cast Film | 450 | MPa | MA 18068 |
| Tensile Strength 2 | |||
| MD : Yield, 50 µm, Cast Film | 19.4 | MPa | ASTM D882 |
| MD : Break, 50 µm, Cast Film | 38.0 | MPa | ASTM D882 |
| MD : Break, 50 µm, Cast Film | 37.0 | MPa | MA 18068 |
| TD : Break, 50 µm, Cast Film | 34.0 | MPa | MA 18068 |
| Tensile Elongation 3 | |||
| MD : Break, 50 µm, Cast Film | 740 | % | ASTM D882 |
| MD : Break, 50 µm, Cast Film | 850 | % | MA 18068 |
| TD : Break, 50 µm, Cast Film | 900 | % | MA 18068 |
| Dart Drop Impact (Cast Film) | 500 | g | MA 17106 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| 0°C | 2.5 | kJ/m² | |
| 23°C | 10 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 60.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 125 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Cast Film) | 85 | ISO 2813 | |
| Haze (50.0 µm, Cast Film) | < 1.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 30 mm/min |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unichem 8818 | Colorite Polymers | PVC, Unspecified | Unichem |
| GAPEX® HPP30GR33NA | Ferro Corporation | PP Homopolymer | GAPEX® |
| LNP™ LUBRICOMP™ RFL36 compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |
| Hostacom PPU X9067HS 4PK SOUL | LyondellBasell Industries | PP, Unspecified | Hostacom |
| LEXAN™ SLX2271T resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |