Prime ABS Weather-X 200

Category:	ABS+Acrylic , Acrylonitrile Butadiene Styrene + Acrylic (PMMA)
Manufacturer:	Primex Plastics Corporation
Trademark:	Prime ABS Weather-X
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	tE6tkA_Prime-ABS-Weather-X-200.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Is an acrylic capped co-extruded ABS sheet, which can be produced as a two or three multilayer composite. The acrylic cap imparts a very high gloss, vibrant colors with superior depth of image, excellent UV protection, chemical resistance, toughness and excellent formability. Applications: The performance features of Prime ABS Weather-X 200 make it the material of choice for applications, including marine, personal watercraft, recreational vehicles, lawn/garden, building/construction and automotive accessories. Processing: Surface Temp = 325-360°F Mold Temp = 150-175°F De-mold @ 170°F Mold shrink is .004-.008 in/in. ABS may absorb greater amounts of radiant energy than acrylic; thus, surface temperatures may increase more rapidly. Care should be taken to maintain the surface temperature at 325°F-360°F to avoid blistering, burning and color/gloss shift of the acrylic cap. Finishing: Prime ABS Weather-X 200 can be joined using mechanical methods such as bolts, screws or clamps, or chemical methods such as cementing. When drilling coextruded sheet with an acrylic modified drill bit, be sure to exit from the acrylic side but when drilling with a standard bit, be sure to have the bit exit from the substrate side. For accuracy and safety, Prime ABS Weather-X 200 should be clamped during drilling. Please contact your Primex Plastics representative for more information on finishing, fabricating, or the thermoforming process. Colors, Textures and Capabilities: Prime ABS Weather-X 200 can be color matched to meet your specific requirements. The surface is typically high gloss but textures such as calf grain, H/C, F/L H/C, Levant 1 and Seville are available.

Message

Is an acrylic capped co-extruded ABS sheet, which can be produced as a two or three multilayer composite. The acrylic cap imparts a very high gloss, vibrant colors with superior depth of image, excellent UV protection, chemical resistance, toughness and excellent formability.

Applications:
The performance features of Prime ABS Weather-X 200 make it the material of choice for applications, including marine, personal watercraft, recreational vehicles, lawn/garden, building/construction and automotive accessories.

Processing:
Surface Temp = 325-360°F
Mold Temp = 150-175°F
De-mold @ 170°F
Mold shrink is .004-.008 in/in.
ABS may absorb greater amounts of radiant energy than acrylic; thus, surface temperatures may increase more rapidly. Care should be taken to maintain the surface temperature at 325°F-360°F to avoid blistering, burning and color/gloss shift of the acrylic cap.

Finishing:
Prime ABS Weather-X 200 can be joined using mechanical methods such as bolts, screws or clamps, or chemical methods such as cementing. When drilling coextruded sheet with an acrylic modified drill bit, be sure to exit from the acrylic side but when drilling with a standard bit, be sure to have the bit exit from the substrate side. For accuracy and safety, Prime ABS Weather-X 200 should be clamped during drilling.

Please contact your Primex Plastics representative for more information on finishing, fabricating, or the thermoforming process.

Colors, Textures and Capabilities:
Prime ABS Weather-X 200 can be color matched to meet your specific requirements. The surface is typically high gloss but textures such as calf grain, H/C, F/L H/C, Levant 1 and Seville are available.

General Information
Additive	UV Stabilizer
Features	Good Chemical Resistance Good Color Stability Good Moldability Good UV Resistance High Gloss High Heat Resistance High Impact Resistance High Tensile Strength
Uses	Automotive Applications Building Materials Construction Applications Lawn and Garden Equipment Marine Applications Sporting Goods Water Sports Equipment
Appearance	Colors Available
Forms	Sheet

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.05	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (230°C/3.8 kg)	8.9	g/10 min	ASTM D1238
Molding Shrinkage - Flow	0.30 to 0.50	%	ASTM D955

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Break)	36.0	MPa	ASTM D638
Tensile Elongation (Break)	22	%	ASTM D638
Flexural Modulus	1930	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact			ASTM D256
0°C, 3.18 mm	230	J/m
22°C, 3.18 mm	300	J/m

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm)	97.8	°C	ASTM D648

Optical	Nominal Value		Test Method
Gardner Gloss (60°)	87		ASTM D523

Additional Information	Nominal Value	Unit
De-mold Temperature	77	°C
Mold Temperature (other)	66 to 79	°C
Surface Temperature	163 to 182	°C

Resin Grade	Manufacturer	Category	Trademark
SEQUEL® 1780	LyondellBasell Industries	TPO (POE)	SEQUEL®
TAROMID B 280 Z1 G6	Taro Plast S.p.A.	Nylon 6	TAROMID B
Vinnolit® MP 8058	Vinnolit GmbH & Co. KG	PVC Homopolymer	Vinnolit®
Clariant PC PC-000-L	Clariant Corporation	PC	Clariant PC
DOWLEX™ 2256G	The Dow Chemical Company	LLDPE	DOWLEX™