Mar-Bal MB3000-20NY
| Category: | Polyester, TP , Thermoplastic Polyester |
| Manufacturer: | Mar-Bal, Inc. |
| Trademark: | Mar-Bal |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tDeF0i_Mar-Bal-MB3000-20NY.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A superior chemical resistant material with excellent flame and track resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.75 to 1.85 | g/cm³ | ASTM D792 |
| Bulk Factor | 1.5 to 2.0 | ASTM D1895 | |
| Molding Shrinkage - Flow | 0.050 to 0.15 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.12 | % | ASTM D570 |
| Color 1 | |||
| Change Under Heat (Bisque) : 149°C | 1.0 to 1.5 | ||
| Change Under Heat (White) : 149°C | 1.2 to 1.7 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 45 to 55 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 41.4 to 62.1 | MPa | ASTM D638 |
| Flexural Modulus | 12400 to 13100 | MPa | ASTM D790 |
| Flexural Strength | 124 to 145 | MPa | ASTM D790 |
| Compressive Modulus | 345000 to 379000 | MPa | ASTM D695 |
| Compressive Strength | 96.5 to 110 | MPa | ASTM D695 |
| Shear Strength | 55.2 to 62.1 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 430 to 750 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | > 260 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 2 | > 14 | kV/mm | ASTM D149 |
| Arc Resistance | > 185 | sec | ASTM D495 |
| Inclined-Plane Tracking | > 1000 | min | ASTM D2303 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 5V | UL 94 |
| Note Message | |
|---|---|
| 1 . | 300 hrs |
| 2 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ PA6G30-BK | Pier One Polymers, Inc. | Nylon 6 | MAXAMID™ |
| APICAL 200AV | Kaneka Corporation | Film, PI | APICAL |
| OmniCarb™ PC/ABS 912 LG UV | OMNI Plastics, LLC | PC+ABS | OmniCarb™ |
| Plasmer 1050DN/1002 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |
| LNP™ LUBRICOMP™ KL003 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |