NYLOY® MG-0833B
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Nytex Composites Co., Ltd. |
| Trademark: | NYLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tBtQG9_NYLOY-MG-0833B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NYLOY® MG-0833B is a Polyamide 66 (Nylon 66) material filled with 33% glass fiber. It is available in Asia Pacific or North America for injection molding. Primary attribute of NYLOY® MG-0833B: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.18 | g/cm³ | ASTM D792 |
| -- | 1.39 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow | 0.34 | % | |
| Across Flow | 1.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 114 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 137 | MPa | ASTM D638 |
| -- | 125 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 2.0 | % | ASTM D638 |
| Break | 1.9 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 7850 | MPa | ASTM D790 |
| -- | 8000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 196 | MPa | ASTM D790 |
| -- | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.8 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 3.18 mm) | 78 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 235 | °C | |
| 1.8 MPa, Unannealed | 225 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 270 to 300 | °C | |
| Mold Temperature | 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 3M™ Dyneon™ Fluoroplastic FEP 6322HTZ | 3M Advanced Materials Division | FEP | 3M™ Dyneon™ Fluoroplastic |
| Hostacom EKC 330NA | LyondellBasell Industries | PP, Unspecified | Hostacom |
| Ixef® BXT 2000-0203 | Solvay Specialty Polymers | PARA | Ixef® |
| Politer 50 GF | Poliblend S.p.a. | PBT | Politer |
| LNP™ LUBRILOY™ RF208 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRILOY™ |