Order Products : sales@su-jiao.com
Sasol Polymers PE HF125
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Sasol Polymers |
| Trademark: | Sasol Polymers PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tBYw7c_Sasol-Polymers-PE-HF125.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Features
Applications
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| With itself-dynamic, blown film | 0.33 | ASTM D1894 | |
| With itself-static, blown film | 0.38 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 30 µm, blown film | 12.0 | MPa | ASTM D882 |
| TD : Yield, 30 µm, blown film | 11.0 | MPa | ASTM D882 |
| MD : Broken, 30 µm, blown film | 34.0 | MPa | ASTM D882 |
| TD : Broken, 30 µm, blown film | 25.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield, 30 µm, blown film | 530 | % | ASTM D882 |
| TD : Yield, 30 µm, blown film | 650 | % | ASTM D882 |
| Dart Drop Impact 1(30 µm, Blown Film) | 150 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 30 µm, blown film | 10 | g | ASTM D1922 |
| TD : 30 µm, blown film | 28 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 30 | ASTM D2457 | |
| Haze | 21 | % | ASTM D1003 |
| Additional Information |
|---|
| The above values were calculated from data for 30µm film produced on a 75mm Barmag extruder with 190°C melt temperature using a 2:1 blow ratio and a die gap of 3.0mm. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Hopper Temperature | 180 - 190 | °C | |
| Cylinder Zone 1 Temp. | 190 - 200 | °C | |
| Cylinder Zone 2 Temp. | 190 - 200 | °C | |
| Cylinder Zone 3 Temp. | 190 - 200 | °C | |
| Cylinder Zone 4 Temp. | 190 - 200 | °C | |
| Melt Temperature | 190 | °C | |
| Die Temperature | 190 - 200 | °C |
| Extrusion instructions |
|---|
| Screen Pack: 20/40/20 BS meshBlow ratio: >2:1 |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PPX-FR7 | Polymer Resources Ltd. | PPE+PS | PRL |
| TEKAPPO™ J920 | Mando Advanced Materials Co., Ltd. | PPE+PS | TEKAPPO™ |
| Telcar® TL-8451G | Teknor Apex Company | TPE | Telcar® |
| GAPEX® RPP40EB81HB BLACK | Ferro Corporation | PP Homopolymer | GAPEX® |
| LTM® 318-1B | Cytec Industries Inc. | Epoxy | LTM® |