LUVOCOM® 1100-8401 Datasheet,PESU,Lehmann & Voss & Co.-SHANGHAI SUSHENG

Message
LUVOCOM®1100-8401 is a polyethersulfone (PES) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of 1100-8401 are: Flame Retardant sterilizable Good dimensional stability Typical application areas include: engineering/industrial accessories Electrical/electronic applications Tools Aerospace food contact applications

General Information
Features	Good dimensional stability Disinfect with steam Flame retardancy
Uses	Electrical/Electronic Applications Non-specific food applications Engineering accessories Aerospace applications Machine/mechanical parts Sporting goods Medical/nursing supplies Mold/Mold/Tool
Appearance	Natural color

Physical	Nominal Value	Unit	Test Method
Density	2.17	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (345°C/5.0 kg)	10.0	cm³/10min	ISO 1133
Molding Shrinkage	0.30 - 0.60	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.10	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	5500	MPa	ISO 527-2
Tensile Stress (Break)	80.0	MPa	ISO 527-2
Tensile Strain (Yield)	2.8	%	ISO 527-2
Flexural Modulus	4500	MPa	ISO 178
Flexural Stress	115	MPa	ISO 178
Flexural Strain at Flexural Strength	3.3	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	220	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	> 1.0E+10	ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	4.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	30	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	195	°C	ISO 75-2/A
Continuous Use Temperature	180	°C	UL 746B
Vicat Softening Temperature	215	°C	ISO 306/A

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+10	ohms	IEC 60093

Injection	Nominal Value	Unit
Drying Temperature - Desiccant Dryer	150	°C
Drying Time - Desiccant Dryer	3.0 - 5.0	hr
Suggested Max Moisture	0.050	%
Rear Temperature	355 - 375	°C
Middle Temperature	360 - 380	°C
Front Temperature	350 - 370	°C
Nozzle Temperature	340 - 360	°C
Processing (Melt) Temp	350	°C
Mold Temperature	120 - 200	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.05%, otherwise porosity and surface defects (e.g. smearing) may occur. To avoid internal stresses, a low shear load should be used for processing. The parts may be tempered at a later stage to reduce internal stresses. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.05%, otherwise porosity and surface defects (e.g. smearing) may occur. To avoid internal stresses, a low shear load should be used for processing. The parts may be tempered at a later stage to reduce internal stresses. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Category:	PESU , Polyethersulfone
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	tAbtP9_LUVOCOM-1100-8401.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Sylvin 7833-75 Natural	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
NEO-ZEX™ 2015M	Prime Polymer Co., Ltd.	LLDPE	NEO-ZEX™
HI-ZEX™ 7800M	Prime Polymer Co., Ltd.	HDPE	HI-ZEX™
PERCOM® XG1234	A. Schulman Europe	PP Copolymer	PERCOM®
Dryflex® SE 85A201	ELASTO	TPE	Dryflex®