Hostaform® C 9021 GV3/30 TF2

Category: Acetal (POM) Copolymer , Acetal (POM) Copolymer
Manufacturer: Celanese Corporation
Trademark: Hostaform®
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: t9cwK5_Hostaform-C-9021-GV3-30-TF2.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
Injection molding grade with 30% glass beads, for low warpage parts, slip modified with PTFE
General Information
Filler / Reinforcement
  • Glass Bead, 30% Filler by Weight
Additive
  • PTFE Lubricant
Features
  • Low Warpage
RoHS Compliance
  • Contact Manufacturer
Processing Method
  • Injection Molding
PhysicalNominal ValueUnitTest Method
Density 1.63g/cm³ISO 1183
Melt Volume-Flow Rate (MVR) (190°C/2.16 kg)7.50cm³/10minISO 1133
MechanicalNominal ValueUnitTest Method
Tensile Modulus 3800MPaISO 527-2/1A/1
Tensile Stress (Yield)38.0MPaISO 527-2/1A/50
Tensile Strain (Yield)5.0%ISO 527-2/1A/50
Nominal Tensile Strain at Break 13%ISO 527-2/1A/50
ImpactNominal ValueUnitTest Method
Charpy Notched Impact Strength (23°C)2.5kJ/m²ISO 179/1eA
ThermalNominal ValueUnitTest Method
Melting Temperature 1166°CISO 11357-3
InjectionNominal ValueUnit
Processing (Melt) Temp 190 to 230°C
Mold Temperature 80.0 to 120°C
Screw L/D Ratio 15.0:1.0 to 25.0:1.0
Note Message
1 .10°C/min
Resin Grade Manufacturer Category Trademark
RTP 402 RTP Company PS (GPPS) RTP
Shanghai Ofluorine PVDF T-2 Shanghai Ofluorine Chemical Technology Co., Ltd PVDF Shanghai Ofluorine PVDF
Shinko-Lac® ABS TR-2 Mitsubishi Rayon America Inc. ABS Shinko-Lac®
Badamid® LC70 M40 Bada AG Nylon 6+Nylon 66/6 Badamid®
Badaflex® TPE-S 75A 1205 2K S2 Bada AG SEBS Badaflex®