Tenogel® ABS A3 LF NTLA010 AB348
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Tenogel® ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | t9TwhX_Tenogel-ABS-A3-LF-NTLA010-AB348.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ABS resin for extrusion, excellent mechanical and thermal resistance. |
| General Information | |
|---|---|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 106 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 45.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 50 | % | ASTM D638 |
| Flexural Modulus | 2060 | MPa | ASTM D790 |
| Flexural Strength | 64.0 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dart Drop Test (-40°C) | 24.0 | J | GE |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 8.0 | kJ/m² | |
| 23°C | 16 | kJ/m² | |
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 87 | J/m | |
| 23°C | 280 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 93.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 86.0 | °C | |
| Vicat Softening Temperature | 103 | °C | ASTM D1525 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength | 36 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 2.90 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 9.0E-3 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (2.00 mm) | 700 | °C | IEC 60695-2-12 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2099 X 127618 R | RTP Company | PLA+PC | RTP |
| Baoding 68T85 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyester | Baoding |
| Cheng Yu N66C3 | Cheng Yu Plastic Company Limited | Nylon 66 | Cheng Yu |
| Hylon® N1000EHL2 | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| JSR EPR EP27 | JSR Corporation | EPDM | JSR EPR |