LNP THERMOCOMP PX92248 is a compound based on Nylon 6 resin containing Proprietary Filler(s). Also known as: LNP* THERMOCOMP* Compound PDX-P-92248 Product reorder name: PX92248 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (24 hr) | 0.20 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 8850 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Break | 108 | MPa | |
| Break 2 | 108 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Break | 2.5 | % | |
| Break 3 | 2.5 | % | |
| Flexural Modulus | ASTM D790 | ||
| 50.0 mm Span 4 | 7230 | MPa | |
| -- | 7230 | MPa | |
| Flexural Strength | ASTM D790 | ||
| -- | 179 | MPa | |
| Break, 50.0 mm Span 5 | 179 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 140 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 840 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 196 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 266 to 277 | °C | |
| Front Temperature | 277 to 288 | °C | |
| Processing (Melt) Temp | 266 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shuang-Bang FR-134 | Shuang-Bang Industrial Corp. | PUR, Unspecified | Shuang-Bang |
| LAMIGAMID® 300 | Schwartz Technical Plastic | Nylon 6 | LAMIGAMID® |
| OmniTech™ HDPE TF10 | OMNI Plastics, LLC | HDPE | OmniTech™ |
| Elastoflex® NA 3532/108 Resin / NA 118/4 Isocyanate | BASF Corporation | PUR-MDI | Elastoflex® |
| Sylvin 8950-90 Grey 9415 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |