LNP™ STAT-KON™ DE0049F compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | t8pi9R_LNPSTATKONDE0049Fcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* STAT-KON* DE0049F is a compound based on Polycarbonate resin containing 20% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant, Superior, Molding. Also known as: LNP* STAT-KON* Compound DC-1004 FR SM Product reorder name: DE0049F |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.33 | g/cm³ | ISO 1183, ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.70 - 1.0 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.40 - 0.70 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.13 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.18 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 13400 | MPa | ASTM D638 |
| -- | 15000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 137 | MPa | ASTM D638 |
| Yield | 134 | MPa | ISO 527-2/5 |
| Fracture 3 | 137 | MPa | ASTM D638 |
| Fracture | 134 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.0 | % | ASTM D638 |
| Yield | 1.6 | % | ISO 527-2/5 |
| Fracture 5 | 2.0 | % | ASTM D638 |
| Fracture | 1.6 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 6 | 11600 | MPa | ASTM D790 |
| -- 7 | 11700 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 166 | MPa | ISO 178 |
| Fracture, 50.0mm span 8 | 190 | MPa | ASTM D790 |
| Flexural Strain at Break 9 | 170 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 47 | J/m | ASTM D256 |
| 23°C 10 | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 490 | J/m | ASTM D4812 |
| 23°C 11 | 30 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 146 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 12 | 148 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 143 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 13 | 144 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 1.2E-6 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 60°C | 1.2E-6 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 6.8E-6 | cm/cm/°C | ASTM E831 |
| Lateral : 23 to 60°C | 6.8E-6 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 - 1.0E+3 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 310 - 321 | °C | |
| Front Temperature | 321 - 332 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 82 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 2 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIRASON™ 500BK1 | Mitsui Chemicals, Inc. | LDPE | MIRASON™ |
| NOVADURAN® 5810G40 | Mitsubishi Engineering-Plastics Corp | PBT Alloy | NOVADURAN® |
| Nypol® PA A3 P5 NTLA016 NR345 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Thermec N™ 4340CF10 | Technical Polymers, LLC | PPA | Thermec N™ |
| SABIC® PC PC4800 resin | SABIC Innovative Plastics Asia Pacific | PC | SABIC® PC |