Adiprene® LFG 740D
| Category: | PUR-Ether/TDI , Polyurethane (Polyether, TDI) |
| Manufacturer: | Chemtura |
| Trademark: | Adiprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | t7o4kC_Adiprene-LFG-740D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ADIPRENE LFG 740D is a TDI-terminated polyether prepolymer that, when cured with 4,4'-methylene-bis-(o-chloroaniline),MBCA, yields a 75 Shore D elastomer. The features of ADIPRENE LFG 740D include:
LFG 740D offers improved safety during handling and processing over conventional-type prepolymers due to the low content of free TDI, less than 0.1%. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 75 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Strength | ASTM D695 | ||
| 5% Strain | 8.96 | MPa | |
| 10% Strain | 20.7 | MPa | |
| 15% Strain | 29.6 | MPa | |
| 20% Strain | 39.6 | MPa | |
| 25% Strain | 49.6 | MPa |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Trouser Tear Resistance | 56.0 | N/mm | ASTM D1938 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 26.2 | MPa | |
| 300% Strain | 37.9 | MPa | |
| Tensile Strength | 41.4 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 320 | % | ASTM D412 |
| Tear Strength | |||
| -- 1 | 145 | kN/m | ASTM D624 |
| Split | 19 | kN/m | ASTM D470 |
| Compression Set (70°C, 22 hr) | 50 | % | ASTM D395B |
| Bayshore Resilience | 43 | % | ASTM D2632 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life | 2.0 | min | |
| Demold Time | 30 | min |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Dynamic Properties | |||
| Dynamic Modulus : 30°C | 3.00E+9 | dynes/cm² | |
| Dynamic Modulus : 50°C | 2.20E+9 | dynes/cm² | |
| Dynamic Modulus : 70°C | 1.60E+9 | dynes/cm² | |
| Dynamic Modulus : 130°C | 7.50E+8 | dynes/cm² | |
| Dynamic Modulus : 150°C | 5.90E+8 | dynes/cm² | |
| Tangent : 30°C | 0.0740 | ||
| Tangent : 50°C | 0.0830 | ||
| Tangent : 70°C | 0.0960 | ||
| Tangent : 130°C | 0.0740 | ||
| Tangent : 150°C | 0.0600 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Curing Time (100°C) | 16 | hr |
| Note Message | |
|---|---|
| 1 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8467-94 Black | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |
| Celstran® PP-GF50-0453 P10/10 | Celanese Corporation | PP, Unspecified | Celstran® |
| Hifax TRC 779X | LyondellBasell Industries | TPO (POE) | Hifax |
| HiFill® PA6 0303 B | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Karina GREENY BROWN (SP31456) -E 36/210-GEN | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |