DISTRUMID EC66 GF30
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Distrupol |
| Trademark: | DISTRUMID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | t6KVcc_DISTRUMID-EC66-GF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DISTRUMID EC66 GF30 is a Polyamide 66 (Nylon 66) material filled with 30% glass fiber. It is available in Europe for injection molding. Primary attribute of DISTRUMID EC66 GF30: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.35 | g/cm³ | ISO 1183 |
| Molding Shrinkage (23°C) | 0.25 to 0.55 | % | ISO 2577 |
| Water Absorption (Saturation, 23°C) | 5.5 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 900 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 150 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 9.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 255 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 240 | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 260 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Regrind | 20 | % | |
| Processing (Melt) Temp | 260 to 285 | °C | |
| Mold Temperature | 80.0 to 120 | °C | |
| Back Pressure | 0.300 to 0.500 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Aarolene® AVPS GP 100-1 | Aaron Industries Corp. | PS (GPPS) | Aarolene® |
| Caltex PP M540 | GS Caltex | PP Impact Copolymer | Caltex PP |
| IDI SMC S10 (Glass Content 30%) | IDI Composites International | TS, Unspecified | IDI SMC |
| Sylvin 8600-85 CLEAR | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| OTECH TPE OTO8099 - Profile | OTECH Corporation | TPE | OTECH TPE |