Braskem PE BS002W
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | t6IUYg_Braskem-PE-BS002W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BS002W is a High Density Polyethylene (HDPE), copolymer, that can be used to produce thin walled packages. Offers an outstanding combination of impact resistance and stiffness, excellent stress cracking resistance (ESCR), good reproducibility of the weight of bottles and excellent surface. Application: Blow Molded Small Volume: Bottles for cleaning products, cosmetic products, food and surfactant products. Process: Blow Molding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.959 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.33 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 24 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance | ASTM D1693 | ||
| 2.00mm, 10% Igepal, molded, F50 | 65.0 | hr | ASTM D1693 |
| 2.00mm, 100% Igepal, molded, F50 | 150 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 35.0 | MPa | ASTM D638 |
| Flexural Modulus - 1% Secant (Compression Molded) | 1500 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (Compression Molded) | 300 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Compression Molded) | 84.0 | °C | ASTM D648 |
| Injection instructions |
|---|
| Recommended Blow Molding Conditions: Feeding Zone: 150°C to 160°C Barrel: 160°C to 170°C Die: 170°C to 180°C Mold Temperature: 5°C to 25°C Extruders Equipped with L/D at least equal to 24 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP141 | Southern Polymer, Inc. | PP Homopolymer | PRIMALENE |
| RheTech Polypropylene M20P101-01 | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| Daelim Po1y® DHC-1 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| TECHNYL® A 216 V20 BLACK 21N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |
| LNP™ LUBRICOMP™ ZFL31XXC compound | SABIC Innovative Plastics | PPE+PS | LNP™ LUBRICOMP™ |