Greenflex FD 53 is an ethylene vinyl acetate copolymer (EVA), containing antiblocking agent, for blown film extrusion. Films produced by Greenflex FD 53 exhibit good sealing properties, high flexibility and toughness and optimum processability. Main Application Greenflex FD 53 is recommended for the production of agricultural films and water proofing membrane having outstanding mechanical performances (flexibility, elasticity and adherence) and dimensional stability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.938 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.47 | g/10 min | ISO 1133 |
| Vinyl Acetate Content | 17.0 | wt% | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A, Injection Molded | 90 | ||
| Shore D, Injection Molded | 39 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Recommended / Available | 50 to 200 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : Blown Film | 55.0 | MPa | |
| 1% Secant, TD : Blown Film | 60.0 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, Blown Film | 5.00 | MPa | |
| TD : Yield, Blown Film | 4.50 | MPa | |
| MD : Break, Blown Film | 34.0 | MPa | |
| TD : Break, Blown Film | 32.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, Blown Film | 490 | % | |
| TD : Break, Blown Film | 630 | % | |
| Dart Drop Impact 1(Blown Film) | > 700 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD | 30.0 | kN/m | |
| TD | 50.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 67.0 | °C | ISO 306/A |
| Melting Temperature | 88.0 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, Blown Film) | 65 | ASTM D2457 | |
| Haze (Blown Film) | 6.0 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 to 190 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRISTAR® PC-15R-113 | Polymer Technology and Services, LLC | PC | TRISTAR® |
| YUNGSOX® PP 3064 | Formosa Polypropylene | PP Impact Copolymer | YUNGSOX® PP |
| Daelim Po1y® PP-141 | DAELIM INDUSTRIAL CO., LTD. | PP, Unspecified | Daelim Po1y® |
| LEXAN™ BFL4000U resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Sylvin 8200-88 Green 3186 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |