Geon™ Vinyl Rigid Extrusion L6256
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ Vinyl Rigid Extrusion |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | t5u82x_Geon-Vinyl-Rigid-Extrusion-L6256.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Geon™ Vinyl Rigid Extrusion L6256 is a Rigid Polyvinyl Chloride product. It can be processed by extrusion and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Applications of Geon™ Vinyl Rigid Extrusion L6256 include plumbing/piping/potable water and wire & cable. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| PVC Cell Classification | 16364 | ASTM D1784 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3060 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 42.3 | MPa | ASTM D638 |
| Flexural Modulus | 2660 | MPa | ASTM D790 |
| Flexural Strength | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256A | ||
| -18°C, 3.18 mm, Compression Molded 3 | 120 | J/m | |
| 0°C, 3.18 mm, Compression Molded 4 | 880 | J/m | |
| 23°C, 3.18 mm, Compression Molded 5 | 1200 | J/m | |
| Instrumented Dart Impact 6 | ASTM D3763 | ||
| -18°C, 1.85 mm, brittle | 19.8 | J | |
| 0°C, 1.85 mm, brittle | 21.9 | J | |
| 23°C, 1.85 mm, ductile | 25.1 | J | |
| Drop Impact Resistance | ASTM D4226 | ||
| 23°C 7 | 66.7 | J/cm | |
| 23°C 8 | > 178 | J/cm |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 77.7 | °C | |
| 0.45 MPa, Annealed | 80.0 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 74.5 | °C | |
| 1.8 MPa, Annealed | 78.0 | °C | |
| CLTE - Flow | 6.3E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.701 mm, ALL | V-0 | ||
| 3.00 mm, ALL | 5VA |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Ease of Sizing | Good |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 177 to 188 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| 2 . | Type I, 5.1 mm/min |
| 3 . | all complete breaks |
| 4 . | all hinge breaks |
| 5 . | all hinge breaks |
| 6 . | 3.30 m/sec |
| 7 . | Procedure A, C.125 Dart |
| 8 . | Procedure B, C.125 Dart |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SIBUR Synthetic Rubber NBR 3330 | SIBUR, LLC | NBR | SIBUR Synthetic Rubber |
| Moplen HP741H | LyondellBasell Industries | PP Homopolymer | Moplen |
| THERMOLAST® K TF1STL (Series: FC/S) | KRAIBURG TPE | TPE | THERMOLAST® K |
| YUNTIANHUA® M90 | YunNan YunTianHua Co., Ltd. | Acetal (POM) Copolymer | YUNTIANHUA® |
| LEXAN™ HFD1910 resin | SABIC Innovative Plastics | PC | LEXAN™ |