SEETEC LLDPE UF313
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | SEETEC LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | t5Mo1b_SEETEC-LLDPE-UF313.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
UF313 is manufactured by Unipol process technology. UF313 has good mechanical properties, excellent optical properties and good processability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.1 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 40 µm, Blown Film | 43.1 | MPa | |
| TD : Break, 40 µm, Blown Film | 39.2 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 40 µm, Blown Film | 730 | % | |
| TD : Break, 40 µm, Blown Film | 750 | % | |
| Dart Drop Impact (40 µm, Blown Film) | 150 | g | ASTM D1709 |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 40.0 µm | 49.0 | kN/m | |
| TD : 40.0 µm | 98.1 | kN/m |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 40.0 µm, Blown Film) | 74 | ASTM D2457 | |
| Haze (40.0 µm, Blown Film) | 11 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan 2200/B-6027 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyester | Xuchuan |
| Unichem 8011G-05 | Colorite Polymers | PVC, Unspecified | Unichem |
| Cri-Line LC-508-55 | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| LNP™ LUBRICOMP™ RL003 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |
| Versaflex™ CL2000X | PolyOne Corporation | TPE | Versaflex™ |