LEXAN™ FXD104R resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | t4qIfG_LEXAN-FXD104R-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FXD104R is a Light Diffusion effect, which is part of the VisualFX family. Color Package may affect properties. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/3.8 kg) | 7.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (220°C/5.0 kg) | 6.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.35 | % | |
| Equilibrium, 23°C, 50% RH | 0.15 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2300 | MPa | ASTM D638 |
| -- | 2350 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 62.0 | MPa | ASTM D638 |
| Yield | 63.0 | MPa | ISO 527-2/50 |
| Break 3 | 69.0 | MPa | ASTM D638 |
| Break | 70.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 7.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Break 5 | 120 | % | ASTM D638 |
| Break | 120 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2370 | MPa | ASTM D790 |
| -- 7 | 2300 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 90.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 94.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 15 | kJ/m² | |
| 23°C | 75 | kJ/m² | |
| Charpy Unnotched Impact Strength 10 | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | |||
| -30°C | 140 | J/m | ASTM D256 |
| 23°C | 900 | J/m | ASTM D256 |
| -30°C 11 | 12 | kJ/m² | ISO 180/1A |
| 23°C 12 | 70 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 13 | ISO 180/1U | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Instrumented Dart Impact (23°C, Total Energy) | 63.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 126 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 14 | 127 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 154 | °C | ASTM D1525 15 |
| -- | 144 | °C | ISO 306/B50 |
| -- | 145 | °C | ISO 306/B120 |
| CLTE | |||
| Flow : -40 to 40°C | 7.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 7.1E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 7.0E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 7.2E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 270 to 300 | °C | |
| Middle Temperature | 280 to 310 | °C | |
| Front Temperature | 290 to 320 | °C | |
| Nozzle Temperature | 280 to 310 | °C | |
| Processing (Melt) Temp | 290 to 320 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*3 sp=62mm |
| 10 . | 80*10*3 sp=62mm |
| 11 . | 80*10*3 |
| 12 . | 80*10*3 |
| 13 . | 80*10*3 |
| 14 . | 120*10*4 mm |
| 15 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP EMI 362 | RTP Company | PC | RTP |
| Retpol® CD 10 HS UV3 | PolyPacific Pty. Ltd. | PP Copolymer | Retpol® |
| HiFill® PPSU 4000 BK | Techmer Engineered Solutions | PPSU | HiFill® |
| Lupoy® 1603-03 | LG Chem Ltd. | PC | Lupoy® |
| OMIKRON BGT 50 NAT | TECNOPOL | PP Copolymer | OMIKRON |