Generic PPC
| Category: | PPC , Polyphthalate Carbonate |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | t3ZQrx_Generic-PPC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PPC This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 2.0 - 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 0.75 - 0.90 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.16 - 0.19 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 85 - 127 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Yield, 23°C | 65.0 - 65.1 | MPa | ISO 527-2 |
| Fracture, 23°C | 71.7 - 77.9 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 78 - 120 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2030 - 2330 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C) | 95.1 - 97.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 370 - 640 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 3200 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 143 - 149 | °C | ASTM D648 |
| Vicat Softening Temperature | 154 - 167 | °C | ISO 306 |
| CLTE - Flow | 6.0E-5 - 9.2E-5 | cm/cm/°C | ASTM E831 |
| Specific Heat (23°C) | 1260 | J/kg/°C | ASTM C351 |
| RTI Elec | 125 - 130 | °C | UL 746 |
| RTI Imp | 125 - 130 | °C | UL 746 |
| RTI | 125 - 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 2.6E+16 - 2.6E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C) | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C) | 3.00 - 3.27 | ASTM D150 | |
| Dissipation Factor (23°C) | 1.2E-3 - 0.024 | ASTM D150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 327 - 338 | °C | |
| Middle Temperature | 338 - 349 | °C | |
| Front Temperature | 349 - 360 | °C | |
| Nozzle Temperature | 343 - 354 | °C | |
| Processing (Melt) Temp | 349 - 360 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PPCThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2920-90 Clear | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Terralene® LL 1101 | FKuR Kunststoff GmbH | HDPE+LLDPE | Terralene® |
| TORZEN® G3300HSL NC01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| ELASTOSIL® M 4601 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® M |
| IPC PP 4810H-T | International Polymers Corporation | PP Homopolymer | IPC PP |