PEARLCOAT® 162K
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | PEARLCOAT® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | t30AKh_PEARLCOAT-162K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PEARLCOAT® 162K is a polyether-based TPU, supplied in form of translucent, colourless pellets, combining hardness with excellent low-temperature flexibility and very good hydrolysis resistance. PEARLCOAT® 162K is used in melt coatings on textile substrates, for end-uses in industrial coatings (for life-jackets, etc.) obtained by extrusion and calendering. PEARLCOAT® 162K is used for obtaining extruded films and fabric coatings. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792, DIN 53479 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 82 | ASTM D2240, DIN 53505 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 25.0 | mm³ | DIN 53516 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Extruder Screw L/D Ratio | 25:1 | ||
| Extruder Screw Compression Ratio | 3:1 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| 100% strain | 5.01 | MPa | ASTM D412 |
| 100% strain | 5.00 | MPa | DIN 53504 |
| 300% strain | 10.0 | MPa | ASTM D412, DIN 53504 |
| Tensile Strength | |||
| Yield | 30.1 | MPa | ASTM D412 |
| Yield | 30.0 | MPa | DIN 53504 |
| Tensile Elongation (Break) | 550 | % | ASTM D412, DIN 53504 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -42.2 | °C | DIN 51007 |
| Melting Temperature 1 | 143 - 154 | °C | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 100 | °C | |
| Drying Time | 2.0 | hr | |
| Cylinder Zone 1 Temp. | 160 - 170 | °C | |
| Cylinder Zone 2 Temp. | 170 - 180 | °C | |
| Cylinder Zone 3 Temp. | 180 - 190 | °C | |
| Cylinder Zone 4 Temp. | 185 - 195 | °C | |
| Die Temperature | 185 - 195 | °C |
| Extrusion instructions |
|---|
| Cooling: AirSpeed: 50 rpmThickness Die: 0.2 mm |
| Note Message | |
|---|---|
| 1 . | Temperature at which MFI = 10 g/10 min @ 21.6 kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XAREC™ S105 | Idemitsu Kosan Co., Ltd. | SPS | XAREC™ |
| FRblend® PP-1303 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PP, Unspecified | FRblend® |
| INEOS LLDPE LL6910KJ | INEOS Olefins & Polymers Europe | LLDPE | INEOS LLDPE |
| INLUBE PPGF20TF15HSFC | Infinity LTL Engineered Compounds | PP, Unspecified | INLUBE |
| Karina IVORY PVC COMPOUND 807D35/ 1-C-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |