HiFill® PC/PBT IM 5720 LE
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | t2ivGX_HiFill-PC-PBT-IM-5720-LE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HiFill®PC/PBT IM 5720 LE is a polycarbonate polybutene terephthalate (PC PBT) product,. It can be processed by injection molding and is available in North America. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 48.3 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 160 | % | ASTM D638 |
| Flexural Modulus | 2000 | MPa | ASTM D790 |
| Flexural Strength | 75.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -23°C, 3.18 mm | 270 | J/m | ASTM D256 |
| 23°C, 3.18 mm | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 118 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 98.9 | °C | ASTM D648 |
| CLTE - Flow | 2.3E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.57 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 98.9 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 238 - 266 | °C | |
| Middle Temperature | 238 - 266 | °C | |
| Front Temperature | 238 - 266 | °C | |
| Processing (Melt) Temp | 238 - 266 | °C | |
| Mold Temperature | 54.4 - 93.3 | °C | |
| Back Pressure | 0.172 - 0.414 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® Vestolen A 5061R 65308 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® Vestolen A |
| UBE Nylon 1022 C2 | UBE Engineering Plastics, S.A. | Nylon 6 | UBE Nylon |
| FERREX® GPP30CN33HB-NA | Ferro Corporation | PP, Unspecified | FERREX® |
| Hyundai EP Breathable AT850/2102 | HYUNDAI EP Co., Ltd. | Polyolefin, Unspecified | Hyundai EP Breathable |
| DURANEX® CTN7133N/B | Polyplastics Co., Ltd. | PBT | DURANEX® |