Noryl* FE1740PW Polyphenylene Oxide (PPO) + Polystyrene (PS) resin is a 40% Glass Reinforced, injection moldable grade with improved hydrolytic stability and with a Tensile Modulus >11000 MPa; this grade has been developed for fluid engineering applications where higher static stiffness is required. Noryl* FE1740PW has been certified for potable water applications up to 85C in Europe and North America in limited colours. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 10 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/10.0 kg) | 20.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.090 - 0.15 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.20 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.060 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 13800 | MPa | ASTM D638 |
| -- | 11300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture 2 | 165 | MPa | ASTM D638 |
| Fracture | 155 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 3 | 1.8 | % | ASTM D638 |
| Fracture | 1.8 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 4 | 11700 | MPa | ASTM D790 |
| -- 5 | 9500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 195 | MPa | ISO 178 |
| Fracture, 50.0mm span 6 | 225 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength 7(23°C) | 30 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 90 | J/m | ASTM D256 |
| 23°C | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact Strength 8 | ISO 180/1U | ||
| -30°C | 30 | kJ/m² | ISO 180/1U |
| 23°C | 30 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 18.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 148 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 9 | 147 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 151 | °C | ASTM D1525 10 |
| -- | 152 | °C | ISO 306/B50 |
| -- | 161 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : -40 to 40°C | 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 250 - 270 | °C | |
| Middle Temperature | 270 - 290 | °C | |
| Front Temperature | 290 - 310 | °C | |
| Nozzle Temperature | 280 - 300 | °C | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 sp=62mm |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PPR PA6601 | Premier Plastic Resins, Inc. | Nylon 66 | PPR |
| RAYPRENE® NB221-S4043 | R&P (Pte.) Ltd. | TPE | RAYPRENE® |
| Sylvin 2900-65 Clear | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Plaslube® HO TL15 | Techmer Engineered Solutions | Acetal (POM) Homopolymer | Plaslube® |
| LGE 555SE | LG Polymers India Pvt. Ltd. | PS (EPS) | LGE |