LNP™ VERTON™ NV003E compound
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | t1isVH_LNPVERTONNV003Ecompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON NV003E is a compound based on PC+ABS Blend resin containing Long Glass Fiber. Added features of this material include: Easy Molding. Also known as: LNP* VERTON* Compound PCA-F-7003 EM Product reorder name: NV003E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5770 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 112 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2 |
| Flexural Modulus | 5680 | MPa | ISO 178 |
| Flexural Stress | 162 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 1 | ISO 180/1A | ||
| -40°C | 23 | kJ/m² | ISO 180/1A |
| 23°C | 21 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 18.5 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 2(1.8 MPa, Unannealed, 64.0 mm Span) | 136 | °C | ISO 75-2/Af |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UmaPET AOCMH | Ester Industries Ltd. | PET | UmaPET |
| Adsyl 5 C 33 F | LyondellBasell Industries | Polyolefin, Unspecified | Adsyl |
| Electrafil® PS-31/EC | Techmer Engineered Solutions | PS (GPPS) | Electrafil® |
| EL-Lene™ L2009FA | SCG Chemicals Co., Ltd. | LLDPE | EL-Lene™ |
| DAI-EL™ G-501NK | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |