HOPELEN L-670M
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | HOPELEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | t1UC6O_HOPELEN-L-670M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
L-670M is a polypropylene random copolymer manufactured by under the Spheripol process. This grade is designed to potential end use applications include Extrusion coating on BOPP film. Good stiffness, Good processability, Good pigment dispersion, Good bond strength |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 28 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 101 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 22.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 500 | % | ASTM D638 |
| Flexural Modulus | 785 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 57 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 65.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 126 | °C | ISO 306 |
| Melting Temperature | 145 | °C | Internal Method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYshine PBT D234 GF30 FR | Polykemi AB | PBT | POLYshine |
| RTP 1399 X 115071 B | RTP Company | PPS | RTP |
| RTP ESD C 700 A | RTP Company | LDPE | RTP |
| Bergamid™ NI-15GF/000 FR GR002 | PolyOne Corporation | Nylon 610 | Bergamid™ |
| LOTTMER SH-070AB | Lotte Chemical Corporation | SEBS | LOTTMER |