LNP™ KONDUIT™ PX11311 compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ KONDUIT™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | t1P1bM_LNP-KONDUIT-PX11311-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Thermally conductive mineral filled PA6 FR compound Also known as: LNP* KONDUIT* Compound PX11311 Product reorder name: PX11311 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.74 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (300°C/10.0 kg) | 49.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.33 | % | |
| Across Flow : 24 hr | 0.48 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 0.25 | % | Internal Method |
| Equilibrium, 23°C, 50% RH | 0.040 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 7240 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 52.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 9050 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 50.0 mm Span) | 76.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 5.3 to 18 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 180 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 199 | °C | ASTM D648 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 3.1E-5 | cm/cm/°C | |
| Flow : 40 to 120°C | 1.9E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 4.6E-5 | cm/cm/°C | |
| Transverse : 40 to 120°C | 7.0E-5 | cm/cm/°C | |
| Specific Heat | 1420 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | |||
| -- 6 | 1.2 | W/m/K | ASTM E1461 |
| -- 7 | 2.1 | W/m/K | ASTM E1461 |
| -- 8 | 0.99 | W/m/K | ISO 22007-2 |
| -- 9 | 1.4 | W/m/K | ISO 22007-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | ASTM D257 |
| Dielectric Strength (1.00 mm, in Oil) | > 10 | kV/mm | ASTM D149 |
| Dielectric Constant (1.10 GHz) | 4.74 | ASTM ES7-83 | |
| Dissipation Factor (1.10 GHz) | 7.7E-3 | ASTM ES7-83 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.00 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 775 | °C | |
| 3.00 mm | 850 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 260 to 275 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 85.0 to 100 | °C | |
| Back Pressure | 0.200 to 0.300 | MPa | |
| Screw Speed | 20 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | through-plane, 10*10*3mm sample |
| 7 . | in-plane, ø25*0.4mm disc |
| 8 . | through-plane, ø80*3mm discs |
| 9 . | in-plane, ø80*3mm discs |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 6 FRB 4 | Plastcom | Nylon 6 | SLOVAMID® 6 |
| Sylvin 5190-80 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 8673-70 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Allen ABS AX7/LXS | SEKISUI Polymer Innovations, LLC | ABS | Allen ABS |
| SQUARE® LIM2012-40A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |