RTP 2283
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | t13HEb_RTP-2283.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 to 0.20 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.16 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 17900 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 186 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.6 | % | ASTM D638 |
| Flexural Modulus | 13800 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 283 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 59 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 530 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 288 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+2 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 357 to 399 | °C | |
| Middle Temperature | 366 to 418 | °C | |
| Front Temperature | 385 to 427 | °C | |
| Mold Temperature | 121 to 204 | °C | |
| Injection Pressure | 68.9 to 124 | MPa | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 60 to 90 | rpm | |
| Clamp Tonnage | 6.9 to 11 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOYOBO Urethane A2080A | TOYOBO America, Inc. | PUR-Capro | TOYOBO Urethane |
| Trademark PE HDP0353 | Trademark Plastics Corporation | HDPE | Trademark PE |
| 4MID® 9A22110 I | 4Plas | Nylon 66 | 4MID® |
| Bayblend® T90 HT | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| Laticonther 82 CP1/800 | LATI S.p.A. | Nylon 12 | Laticonther |