Infino ASF-9810F
| Category: | PBT+PET , Polybutylene Terephthalate + PET |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | szou6w_Infino-ASF-9810F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Material for automobile lamp with high flowability |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 55 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955, ISO 2577 | ||
| Flow : 3.20 mm | 1.6 | % | |
| Across Flow : 3.20 mm | 1.6 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2350 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 1 | 59.0 | MPa | ASTM D638 |
| Yield | 58.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 2 | 15 | % | ASTM D638 |
| Break | 15 | % | ISO 527-2/50 |
| Flexural Modulus 3 | |||
| -- | 2500 | MPa | ASTM D790 |
| -- | 2320 | MPa | ISO 178 |
| Flexural Stress 4 | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 5(23°C) | 3.7 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact Strength 6(23°C) | 4.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 4.00 mm | 130 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 4.00 mm | 60.0 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 120 | °C | |
| Desiccant Dryer | 120 | °C | |
| Drying Time | |||
| -- | > 4.0 | hr | |
| Desiccant Dryer | > 4.0 | hr | |
| Suggested Max Moisture | < 0.10 | % | |
| Rear Temperature | 210 to 220 | °C | |
| Middle Temperature | 230 to 240 | °C | |
| Front Temperature | 250 to 260 | °C | |
| Nozzle Temperature | 260 | °C | |
| Mold Temperature | 30.0 to 60.0 | °C | |
| Injection Pressure | 88.3 | MPa | |
| Back Pressure | 0.981 to 1.96 | MPa | |
| Screw Speed | 30 to 80 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | Thickness: 4 mm |
| 6 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polyethylene HDPE MS 201 BN-NA (EU) | TOTAL Refining & Chemicals | HDPE, HMW | TOTAL Polyethylene |
| Nymax™ GMF 604 40 UV Black 148 | PolyOne Corporation | Nylon 6 | Nymax™ |
| CALP WS641 | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| Gallonprene® GP520-9001 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| GELAST GT80IT | Guang Sung Plastics (GSPL) | TP, Unspecified | GELAST |