Macromeric® 0103-212b BK
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | Saco Polymers |
| Trademark: | Macromeric® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sz6p9q_Macromeric-0103-212b-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Non-halogen flame retardant compound Macromeric ® 0103-212bBK is a black, UV resistant, non-halogen flame retardant RoHS polyolefin compound. It is designed for use in a wide variety of jacketing applications including wire and cable and tube bundles. This compound has superior fire performance; including slow flame propagation, self-extinguishing characteristics, and low smoke production. Macromeric ® 0103-212bBK should be extruded with a screw configuration designed to optimize process conditions and throughput. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.47 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 16 | g/10 min | ASTM D1238 |
| Ash Content - Procedure B | 44 | % | ASTM D5630 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deformation - 2000-gram load (100°C) | 5.0 | % | UL 1277 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Smoke Density | ASTM E662 | ||
| Flaming Mode | 30 | Ds | |
| Smoldering Mode | 230 | Ds |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 171 to 182 | °C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 1 sec) | 95 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 13.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 200 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 186 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength (23°C) | 56.0 | kN/m | ASTM D470 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (121°C, 168 hr) | 5.0 | % | ASTM D638 |
| Change in Ultimate Elongation in Air (121°C, 168 hr) | -15 | % | ASTM D638 |
| Change in Tensile Strength (70°C, 4 hr, in Oil) | -15 | % | ASTM D638 |
| Change in Ultimate Elongation (70°C, 4 hr, in Oil) | -5.0 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature 2 | -35.0 | °C | ASTM D746 |
| UL Temperature Rating 3 | 90 | °C | UL 1581 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index 4 | 35 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 6.0 to 8.0 | hr | |
| Cylinder Zone 1 Temp. | 149 to 160 | °C | |
| Cylinder Zone 2 Temp. | 166 to 177 | °C | |
| Cylinder Zone 3 Temp. | 177 to 188 | °C | |
| Cylinder Zone 4 Temp. | 177 to 188 | °C | |
| Melt Temperature | 182 to 193 | °C | |
| Die Temperature | 188 to 199 | °C |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 3 minutes in methanol |
| 3 . | Test Conditions: Air, 150-days at 97°C |
| 4 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Star L POM D74 | Eurostar Engineering Plastics | Acetal (POM) Copolymer | Star L |
| VITAMIDE® BF23RD6633 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| DOW鈩?Adhesive Film (DAF) 780 | The Dow Chemical Company | Polyolefin, Unspecified | DOW鈩?Adhesive Film (DAF) |
| Fluoroplex GF 515 - GML | UNIFLON | PTFE | Fluoroplex |
| Elastocon® 2865ST | Elastocon TPE Technologies | TPE | Elastocon® |