DINAPLEN® PPH1S25 C20-4152
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Grupo Repol |
| Trademark: | DINAPLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | syrrTp_DINAPLEN-PPH1S25-C20-4152.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DINAPLEN® PPH1S25 C20-4152 is a Polypropylene Homopolymer (PP Homopolymer) product filled with 20% carbon fiber. It is available in Europe. Primary characteristic: homopolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.00 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.0 | % | ISO 527-2 |
| Flexural Modulus | 7500 | MPa | ISO 178 |
| Flexural Stress | 75.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 140 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+3 | ohms | ASTM D257 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecomid® NB40 NL RM | Eurotec Engineering Plastics | Nylon 6 | Tecomid® |
| Somos® NanoTool | DSM Somos® | Unspecified | Somos® |
| ULTEM™ VH1003 resin | SABIC Innovative Plastics Asia Pacific | PEI | ULTEM™ |
| ASTALAC™ ABS M7 | Marplex Australia Pty. Ltd. | ABS | ASTALAC™ |
| LNP™ STAT-KON™ KE004 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ STAT-KON™ |