CERTENE™ HPB-0345
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | syMubP_CERTENE-HPB-0345.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HPB-0345 is a certified prime grade Phillips Process BLOW MOLDING copolymer designed to meet end-use requirements of containers for packaging of Household Industrial Chemicals (HIC). HPB-0345 features easy and consistent processability in conventional continuous or intermittent extrusion equipment. It also offers exceptional ESCR and Impact strength. Applications include containers for detergents, bleach, antifreeze, motor oil and agricultural chemicals. HPB-0345 recommended melt temperature is 180 to 200°C, with the mold at 10 to 20°C. HPB-0345 complies with FDA regulation 21CFR 177.1520(c) 3.2(a) and with most international regulations concerning the use of Polyethylene in contact with food articles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.945 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.35 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (100% Igepal, Compression Molded, F50) | > 1000 | hr | ASTM D1693B |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Compression Molded) | 24.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, Compression Molded) | 900 | % | ASTM D638 |
| Flexural Modulus - Tangent 3(Compression Molded) | 1040 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength (Compression Molded) | 231 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 121 | °C | ASTM D1525 |
| Additional Information |
|---|
| Test specimen was compression molded and was tested according to ASTM D1928 Procedure C. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 10.0 - 20.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 - 200 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALCOM® PA6 900/11 GF10 MR20 SV12-778MCF | ALBIS PLASTIC GmbH | Nylon 6 | ALCOM® PA6 |
| Anjacom® R050/75K | Almaak International GmbH | PC+ABS | Anjacom® |
| HIDEN® M830 | YUHWA Korea Petrochemical Ind. Co., Ltd. | HDPE | HIDEN® |
| POCAN® B 5220 XF 000000 | LANXESS GmbH | PBT | POCAN® |
| CYCOLAC™ INP338T resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |