Amodel® AE-4133
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Amodel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | syEGOn_Amodel-AE-4133.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Amodel AE-4133 is a 33% glass fiber reinforced and hot water formed polyphthalamide (PPA), which is specially used in modern automobile electronic environment. This grade resin is characterized by high thermal deformation temperature, high flexural modulus and high tensile strength, and has good creep resistance and low moisture absorption. -Black: AE-4133 BK902
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.45 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 0.40 | -- | % | ASTM D955 |
| Transverse flow | 0.80 | -- | % | ASTM D955 |
| Water Absorption (24 hr) | 0.23 | -- | % | ASTM D570 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 12000 | -- | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 210 | -- | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.5 | -- | % | ISO 527-2 |
| Flexural Modulus (23°C) | 10700 | -- | MPa | ISO 178 |
| Flexural Stress (23°C) | 295 | -- | MPa | ISO 178 |
| Flexural Strain | 3.1 | -- | % | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 79 | -- | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 9.2 | -- | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 68 | -- | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 300 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature | 95.0 | -- | °C | DSC |
| Melting Temperature | 327 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ASTM E831 | |||
| Flow : 0 to 100°C | 2.0E-5 | -- | cm/cm/°C | ASTM E831 |
| Flow : 100 to 200°C | 1.5E-5 | -- | cm/cm/°C | ASTM E831 |
| Lateral : 0 to 100°C | 7.6E-5 | -- | cm/cm/°C | ASTM E831 |
| Lateral : 100 to 200°C | 1.2E-4 | -- | cm/cm/°C | ASTM E831 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 5.6E+15 | 5.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.20 mm) | 19 | 19 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | |||
| 60 Hz | 4.10 | 4.30 | ASTM D150 | |
| 1 MHz | 3.75 | 3.40 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | |||
| 60 Hz | 6.0E-3 | 0.020 | ASTM D150 | |
| 1 MHz | 0.015 | 0.019 | ASTM D150 | |
| Comparative Tracking Index (CTI) | 600 | 600 | V | UL 746 |
| High Voltage Arc Tracking Rate (HVTR) | 14.0 | 18.0 | mm/min | UL 746 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating 1(3.20 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.030 - 0.060 | % | |
| Rear Temperature | 320 - 330 | °C | |
| Middle Temperature | 320 - 330 | °C | |
| Front Temperature | 327 - 335 | °C | |
| Processing (Melt) Temp | 330 - 345 | °C | |
| Mold Temperature | 65.0 - 95.0 | °C |
| Injection instructions |
|---|
| 射出速度：3-4英寸/秒 (7.5-10 cm/秒)保压压力： 射出压力的50% |
| Note Message | |
|---|---|
| 1 . | These flammability ratings do not represent the risk of these materials or any other materials in actual fire situations. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makroblend® DP7645 | Covestro - Polycarbonates | PC+PET | Makroblend® |
| TECHNYL® 2412GM05-D BLACK | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |
| Sylvin 9077-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| apilon 52c® C 80 | API SpA | TPU-Polyester | apilon 52c® |
| Hostaform® C 13021 10/1570 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |