SABIC® PP 526K
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sxz4CZ_SABIC-PP-526K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PP 526K is a grade developed for efficient thermoforming. SABIC® PP 526K is formulated with a combined processing, antistatic and nucleator package of the next generation. The nucleator technology provides higher stiffness and good transparency/gloss in the thermoformed part. The fact that the polymer/additive package gives higher isotropic processing behaviour reduces warpage, ovality and other dimensional problems. Application: SABIC® PP 526K is typically used for various thermoformed parts sensitive to dimensional stability. Customers use this grade as natural or coloured, ranging from food containers to disposables, yellow fats and lids. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant 1 | 2150 | MPa | ASTM D638 |
| -- | 2050 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield 2 | 40.0 | MPa | ASTM D638 |
| Yield | 40.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 3 | 7.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.5 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 35 | J/m | ASTM D256A |
| 23°C | 3.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 120 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 4 | 115 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 70.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 5 | 65.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 155 | °C | ASTM D1525, ISO 306/A120 6 6 |
| -- | 100 | °C | ASTM D1525, ISO 306/B120 7 7 |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | testbar 80*10*4mm |
| 5 . | testbar 80*10*4mm |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| 7 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SMOKEGUARD™ V 1118 NATURAL | AlphaGary | PVC, Unspecified | SMOKEGUARD™ V |
| Spartech Polycom SCR7-7210 | Spartech Polycom | PC | Spartech |
| Torayca® ASHT-18A | Toray Resin Company | ABS | Torayca® |
| DOWLEX™ HMS 8017 | The Dow Chemical Company | LLDPE | DOWLEX™ |
| Sylvin 9915-55 BLACK | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |