Sindustris ABS LXG679
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sxmpuL_Sindustris-ABS-LXG679.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris ABS LXG679 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific for injection molding. Important attributes of Sindustris ABS LXG679 are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.40 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 114 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 53.0 | MPa | ASTM D638 |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield, 3.20 mm | > 6.0 | % | |
| Break, 3.20 mm | 20 | % | |
| Flexural Modulus 3(3.20 mm) | 2750 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 85.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 3.20 mm | 39 | J/m | |
| -20°C, 6.40 mm | 39 | J/m | |
| 23°C, 3.20 mm | 88 | J/m | |
| 23°C, 6.40 mm | 88 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 86.0 | °C | |
| 0.45 MPa, Unannealed, 6.40 mm | 88.0 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 82.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 83.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Ozone Resistance - 5 sec | No Cracks | JIS K6301 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Rear Temperature | 180 to 200 | °C | |
| Middle Temperature | 190 to 210 | °C | |
| Front Temperature | 200 to 230 | °C | |
| Nozzle Temperature | 200 to 230 | °C | |
| Processing (Melt) Temp | 200 to 230 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 29.4 to 58.8 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 15 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Modified Plastics MPP-S1 | Modified Plastics, Inc. | PP, Unspecified | Modified Plastics |
| SUPRENE® 5206F | SK Global Chemical | EPDM | SUPRENE® |
| XYRON™ X1508 | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| Bayblend® M850 XF | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| HiFill FR® PA6/6 GF25 FR-N IM3 | Techmer Engineered Solutions | Nylon 66 | HiFill FR® |