Sarlink® TPV X5725B
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPV |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sxcHAl_Sarlink-TPV-X5725B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sarlink® TPV X5725B is a Thermoplastic Vulcanizate (TPV) material. It is available in Asia Pacific, Europe, Latin America, or North America. |
| General Information | |
|---|---|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.928 | g/cm³ | ASTM D792 |
| -- | 0.930 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shore A, 5 sec, Extruded | 23 | ||
| Shore A, 5 sec, Injection Molded | 26 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 37 | ||
| Across Flow : 100% Strain | 0.500 | MPa | |
| Flow : 100% Strain | 1.10 | MPa | |
| Tensile Strength | ASTM D412, ISO 37 | ||
| Across Flow : Break | 2.50 | MPa | |
| Flow : Break | 1.50 | MPa | |
| Tensile Elongation | ASTM D412, ISO 37 | ||
| Across Flow : Break | 510 | % | |
| Flow : Break | 200 | % | |
| Tear Strength - Across Flow | |||
| -- | 8.93 | kN/m | ASTM D624 |
| -- 1 | 9.0 | kN/m | ISO 34-1 |
| Compression Set | ASTM D395, ISO 815 | ||
| 23°C, 22 hr | 10 | % | |
| 70°C, 22 hr | 20 | % | |
| 125°C, 70 hr | 51 | % |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air - Across Flow | |||
| 135°C, 1000 hr | -4.0 | % | ASTM D573, ISO 188 |
| 100% Strain, 135°C, 1000 hr | -7.0 | % | ASTM D573 |
| 150°C, 168 hr | -4.0 | % | ASTM D573, ISO 188 |
| 100% Strain, 150°C, 168 hr | -7.0 | % | ASTM D573 |
| 100% Strain 135°C, 1000 hr | -7.0 | % | ISO 188 |
| 100% Strain 150°C, 168 hr | -7.0 | % | ISO 188 |
| Change in Ultimate Elongation in Air - Across Flow | ASTM D573, ISO 188 | ||
| 135°C, 1000 hr | -24 | % | |
| 150°C, 168 hr | -18 | % | |
| Change in Durometer Hardness in Air | ASTM D573, ISO 188 | ||
| Shore A, 135°C, 1000 hr | -1.0 | ||
| Shore A, 150°C, 168 hr | -3.0 | ||
| Change in Volume (125°C, 70 hr, in IRM 903 Oil) | 71 | % | ASTM D471, ISO 1817 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Shear Viscosity - Capillary @ 206/s | |||
| 200°C | 140 | Pa·s | ISO 11443 |
| 200°C | 140 | Pa·s | ASTM D3835 |
| Note Message | |
|---|---|
| 1 . | Method Ba, Angle (Unnicked) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP QR681K | Saudi Basic Industries Corporation (SABIC) | PP Random Copolymer | SABIC® PP |
| Sindustris ABS LSG286 | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Sylvin 8716-95 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TOTAL Polystyrene Impact 830 | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |
| Unipren® Elastomers B3 NTLA010 75A UP311 | Petropol Industry and Trade of Polymers LTDA | PP+EPDM | Unipren® Elastomers |