Celcon® UV25Z
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celcon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sxPWe3_Celcon-UV25Z.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Celcon® UV25Z is a nominal 2.5 melt flow rate acetal copolymer which has been specially stabilized to prevent discoloration and deterioration of mechanical properties from ultraviolet light exposure. The material is available in precolored black or colors. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 2.20 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 2.2 | % | ASTM D955 |
| Transverse flow | 1.8 | % | ASTM D955 |
| Vertical flow direction | 1.7 | % | ISO 294-4 |
| Flow direction | 2.2 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.75 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield, 23°C | 60.7 | MPa | ASTM D638 |
| Yield | 63.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 11 | % | ISO 527-2/1A/50 |
| Flexural Modulus (23°C) | 2420 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 7.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 110 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 90.0 | °C | ISO 75-2/A |
| Melting Temperature | |||
| -- 1 | 166 | °C | ISO 11357-3 |
| -- | 165 | °C | ASTM D3418 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 170 - 180 | °C | |
| Middle Temperature | 180 - 190 | °C | |
| Front Temperature | 180 - 190 | °C | |
| Nozzle Temperature | 190 - 200 | °C | |
| Processing (Melt) Temp | 180 - 200 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 60.0 - 120 | MPa | |
| Injection Rate | Slow | ||
| Holding Pressure | 60.0 - 120 | MPa | |
| Back Pressure | 0.00 - 0.500 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 180 to 200°CZone 4 Temperature: 190 to 200°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRILAC® ABS-HH2350 | Polymer Technology and Services, LLC | ABS | TRILAC® |
| Novamid® 1030J | DSM Engineering Plastics | Nylon 6 | Novamid® |
| 4MID® 9A22150 UV | 4Plas | Nylon 66 | 4MID® |
| BJB Polyurethane TC-865 A/B | BJB Enterprises, Inc. | PUR, Unspecified | BJB Polyurethane |
| Generic ABS - Carbon Fiber | Generic | ABS | Generic |