4DUR® 9K22730
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | 4Plas |
| Trademark: | 4DUR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sxB8H1_4DUR-9K22730.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4DUR 9K22730 is a Standard Flow 30% Carbon Fibre Reinforced PBT |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.14 | % | ISO 62 |
| Moisture Content | < 1000 | ppm | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 24000 | MPa | ISO 527-2/5 |
| Tensile Stress (Break, 23°C) | 150 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 1.5 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C | 7.0 | kJ/m² | ISO 179 |
| 23°C | 8.0 | kJ/m² | ISO 179/B |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 40 | kJ/m² | ISO 179/1eU |
| 23°C | 45 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 6.0 | kJ/m² | ISO 180/1A |
| 23°C | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 40 | kJ/m² | ISO 180/1U |
| 23°C | 45 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature 2 | 225 | °C | ISO 11357 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+3 | ohms | IEC 60093 |
| Volume Resistivity | < 1.0E+3 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 60.0 - 100 | °C | |
| Injection Rate | Fast | ||
| Holding Pressure | 40.0 - 80.0 | MPa | |
| Screw Speed | 200 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 50 - 70 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 24 Hrs |
| 2 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-201-G25 291 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| TECHNYL® A 218 V35 BLACK 21 N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Slique™ 1850W61 Bk-1 | Technical Polymers, LLC | Nylon 6 | Slique™ |
| Bergadur™ PB40 Mi25 natur SO | PolyOne Corporation | PBT | Bergadur™ |
| INELEC PCCF30 | Infinity LTL Engineered Compounds | PC | INELEC |