LNP™ THERMOCOMP™ EX00781H compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sx0rT0_LNP-THERMOCOMP-EX00781H-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP EX00781H is a compoud based on Polyetherimide containng Proprietary Filler(s). Added feature of this material is: Healthcare. Also known as: LNP* THERMOCOMP* Compound PDX-E-00781 EES Product reorder name: EX00781H |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 12 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (340°C/5.0 kg) | 10.4 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3330 | MPa | ASTM D638 |
| -- | 3250 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 91.0 | MPa | ASTM D638 |
| Yield | 91.2 | MPa | ISO 527-2/5 |
| Break 3 | 90.4 | MPa | ASTM D638 |
| Break | 89.7 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 5.9 | % | ASTM D638 |
| Yield | 5.5 | % | ISO 527-2/5 |
| Break 5 | 5.3 | % | ASTM D638 |
| Break | 6.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 3150 | MPa | ASTM D790 |
| -- 7 | 3310 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 148 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 145 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 37 | J/m | ASTM D256 |
| 23°C 9 | 4.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 189 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 190 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 213 | °C | ISO 306/B120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 343 to 354 | °C | |
| Middle Temperature | 354 to 366 | °C | |
| Front Temperature | 366 to 377 | °C | |
| Processing (Melt) Temp | 360 to 366 | °C | |
| Mold Temperature | 121 to 149 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 203 | RTP Company | Nylon 66 | RTP |
| SLOVAMID® 66 T 15 | Plastcom | Nylon 66 | SLOVAMID® 66 |
| Stanyl® TW241F10 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| Electrafil® J-1/CF/30 | Techmer Engineered Solutions | Nylon 66 | Electrafil® |
| StarFlex® 7060-1001 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarFlex® |