Generic TPU-Polyether
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | swzwGw_Generic-TPU-Polyether.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic TPU-Polyether This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.10 - 1.17 | g/cm³ | ASTM D792 |
| 23°C | 1.06 - 1.21 | g/cm³ | ISO 1183 |
| -- | 1110 | kg/m³ | ISO 1183 1 |
| -- | 0.300 - 1.05 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/8.7 kg) | 14 - 24 | g/10 min | ASTM D1238 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.63 - 0.90 | % | ASTM D955 |
| Transverse flow : 23°C | 0.80 - 0.82 | % | ASTM D955 |
| 23°C | 0.80 - 0.81 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| 23°C | 50 - 96 | ASTM D2240 | |
| 23°C | 34 - 98 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 5.52 - 63.6 | MPa | ASTM D638 |
| 23°C | 90.0 - 808 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Fracture, 23°C | 25.0 - 53.1 | MPa | ISO 527-2 |
| 23°C | 1.00 - 44.1 | MPa | ASTM D638 |
| 23°C | 1.00 - 35.2 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture, 23°C | 340 - 610 | % | ASTM D638 |
| Fracture, 23°C | 340 - 800 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 4.83 - 121 | MPa | ASTM D790 |
| 23°C | 18.6 - 193 | MPa | ISO 178 |
| Taber Abrasion Resistance (23°C) | 3.00 - 78.9 | mg | ASTM D1044 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Water Vapor Transmission | 400 - 9100 | g/m²/24 hr | ASTM E96 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Set (23°C) | 6 - 21 | % | ASTM D412 |
| Tensile Stress | |||
| 20% strain, 23°C | 1.99 - 16.5 | MPa | ISO 37 |
| 50% strain, 23°C | 1.10 - 12.3 | MPa | ASTM D412 |
| 100% strain, 23°C | 2.42 - 17.6 | MPa | ASTM D412 |
| 100% strain, 23°C | 2.78 - 25.3 | MPa | ISO 37 |
| 300% strain, 23°C | 4.94 - 36.6 | MPa | ASTM D412 |
| 300% strain, 23°C | 4.80 - 45.0 | MPa | ISO 37 |
| Tensile Strength | |||
| Yield, 23°C | 14.7 - 44.0 | MPa | ASTM D412 |
| Yield, 23°C | 29.5 - 50.7 | MPa | ISO 37 |
| Fracture, 23°C | 23.4 - 56.3 | MPa | ASTM D412 |
| Fracture, 23°C | 25.3 - 51.7 | MPa | ISO 37 |
| 23°C | 24.4 - 50.3 | MPa | ASTM D412 |
| Tensile Elongation | |||
| Fracture, 23°C | 350 - 780 | % | ASTM D412 |
| Fracture, 23°C | 350 - 760 | % | ISO 37 |
| Tensile Elongation at Break | 55 | % | ASTM D412 |
| Tear Strength | |||
| 23°C | 47.6 - 167 | kN/m | ASTM D624 |
| Cracking | 29 | kN/m | ASTM D470 |
| 23°C | 39 - 190 | kN/m | ISO 34-1 |
| Compression Set | |||
| -- | 19 - 47 | % | ASTM D395 |
| 23°C | 20 - 40 | % | ISO 815 |
| Bayshore Resilience | 35 - 51 | % | ASTM D2632 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength (23°C) | -28 - 13 | % | ASTM D471 |
| Change in Volume (23°C) | 0.50 - 36 | % | ASTM D471 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -68.6 - -35.8 | °C | ASTM D746 |
| Glass Transition Temperature | |||
| -- | -48.4 - -13.5 | °C | ASTM E1356 |
| -- | -60.7 - -26.3 | °C | DSC |
| Vicat Softening Temperature | |||
| -- | 66.7 - 145 | °C | ASTM D1525 |
| -- | 75.0 - 139 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 175 - 205 | °C | |
| -- | 134 - 176 | °C | DSC |
| CLTE - Flow | 1.3E-4 - 1.7E-4 | cm/cm/°C | ASTM D696 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | 0.15 - 3.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 54.4 - 115 | °C | |
| Drying Time | 2.0 - 4.1 | hr | |
| Dew Point | -40.0 - -17.8 | °C | |
| Suggested Max Moisture | 3.0E-3 - 0.070 | % | |
| Rear Temperature | 176 - 206 | °C | |
| Middle Temperature | 185 - 206 | °C | |
| Front Temperature | 189 - 221 | °C | |
| Nozzle Temperature | 196 - 231 | °C | |
| Processing (Melt) Temp | 201 - 228 | °C | |
| Mold Temperature | 16.0 - 52.0 | °C | |
| Injection Pressure | 67.3 - 86.3 | MPa | |
| Back Pressure | 0.733 - 5.52 | MPa | |
| Screw Speed | 59 - 130 | rpm | |
| Clamp Tonnage | 5.5 | kN/cm² | |
| Cushion | 3.18 - 3.49 | mm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic TPU-PolyetherThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 54.4 - 117 | °C | |
| Drying Time | 1.9 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 - 0.070 | % | |
| Hopper Temperature | 32.5 - 36.1 | °C | |
| Cylinder Zone 1 Temp. | 169 - 194 | °C | |
| Cylinder Zone 2 Temp. | 177 - 200 | °C | |
| Cylinder Zone 3 Temp. | 177 - 212 | °C | |
| Cylinder Zone 4 Temp. | 179 - 210 | °C | |
| Cylinder Zone 5 Temp. | 180 - 191 | °C | |
| Adapter Temperature | 184 - 211 | °C | |
| Melt Temperature | 189 - 215 | °C | |
| Die Temperature | 189 - 206 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic TPU-PolyetherThis information is provided for comparative purposes only. |
| Note Message | |
|---|---|
| 1 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P2725 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Ravaflex EPM P | Ravago Group | EPM | Ravaflex |
| ColorRx® PE2-0100RX | LTL Color Compounders, Inc. | PE Copolymer | ColorRx® |
| Delrin® 511DP BK402 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| Daelim Po1y® XP5300EN | DAELIM INDUSTRIAL CO., LTD. | mLLDPE | Daelim Po1y® |