Crastin® S600F40 NC010
| Category: | PBT , THERMOPLASTIC POLYESTER RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Crastin® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | swdyT8_Crastin-S600F40-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced Low Viscosity Polybutylene Terephthalate |
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 33 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.8 | % | |
| Flow | 1.9 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 2.00 mm | 0.40 | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.20 | % | |
| Viscosity Number | 120 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2600 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 58.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 30 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 2600 | MPa | |
| 1000 hr | 1800 | MPa | |
| Flexural Modulus | 2400 | MPa | ISO 178 |
| Flexural Stress | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 4.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength (23°C) | 4.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 115 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 180 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 50.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 60.0 | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 55.0 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 175 | °C | ISO 306/B50 |
| Melting Temperature 2 | 225 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.1E-4 | cm/cm/°C | |
| Transverse | 1.2E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 26 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.80 | ||
| 1 MHz | 3.20 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 2.0E-3 | ||
| 1 MHz | 0.020 | ||
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.800 mm | HB | ||
| 1.50 mm | HB | ||
| Oxygen Index | 22 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Melt Density | 1.11 | g/cm³ | |
| Specific Heat Capacity of Melt | 2110 | J/kg/°C | |
| Thermal Conductivity of Melt | 0.21 | W/m/K |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYTROPE® STR 2031REU-01 NATURAL | A. Schulman Inc. | Polyolefin, Enhanced TPO | POLYTROPE® |
| SUPRAN® LFT PA A1350 | SAMBARK | Nylon 66 | SUPRAN® LFT PA |
| VINIKA® CA98HB1 | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| Multi-Flex® TPE A2504 LC | Multibase, A Dow Corning Company | TPE | Multi-Flex® TPE |
| ESTYRENICS 352 | PCC Plastics & Consultations Center | PS (GPPS) | ESTYRENICS |