ENGAGE™ 8100
| Category: | TPO (POE) , Polyolefin Elastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ENGAGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | swbTVq_ENGAGE-8100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ENGAGE™ 8100 Polyolefin Elastomer is an ethylene-octene copolymer that has excellent flow characteristics and performs well in a wide range of general purpose thermoplastic elastomer applications. ENGAGE 8100 provides superb impact properties in blends with polypropylene (PP) and polyethylene (PE). ENGAGE 8100 provides high filler loading capability and outstanding peroxide cure capability. When cross-linked by peroxide, silane, or irradiation, it gives exceptional heat aging, compression set, and weather resistance properties, and may be used to produce high performance electrical insulation. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.870 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Mooney Viscosity (ML 1+4, 121°C) | 24 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 1 sec, Compression Molded | 73 | ||
| Shore D, 1 sec, Compression Molded | 22 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant 1(Compression Molded) | 2.90 | MPa | ASTM D638 |
| Tensile Strength 2(Break, Compression Molded) | 9.76 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Compression Molded) | 810 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant : Compression Molded | 14.3 | MPa | |
| 2% Secant : Compression Molded | 13.1 | MPa |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 4 | 40.0 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -52.0 | °C | Internal Method |
| Vicat Softening Temperature | 45.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) 5 | 60.0 | °C | Internal Method |
| Peak Crystallization Temperature (DSC) | 45.0 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| 4 . | Die C |
| 5 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Veroplas SER80 | PlastxWorld Inc. | ABS | Veroplas |
| ADMER™ AT1955E | Mitsui Chemicals Europe GmbH | TPE | ADMER™ |
| Ferro PP LPP25BC64NA | Ferro Corporation | PP, Unspecified | Ferro PP |
| LARIPUR® LPR 70D60 | COIM S.p.A. | TPU-Polyether | LARIPUR® |
| LEXAN™ CFR5630 resin | SABIC Innovative Plastics | PC | LEXAN™ |