Vyncolit 52-40-40 is a diallyl phthalate (DAP) material containing long glass fiber. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing methods are: resin transfer molding, compression molding or injection molding. The main features of the Vyncolit 52-40-40 are: chemical resistance Good dimensional stability moisture resistance Impact resistance Wear-resistant Typical application areas include: Electrical/electronic applications Wire and cable Aerospace military applications

General Information
Filler / Reinforcement	Long glass fiber
Features	Good dimensional stability Moisture resistance Antibacterial property Solvent resistance Impact resistance, high Good electrical performance Good chemical resistance alkali resistance Good wear resistance Fuel resistance Heat resistance, high acid resistance
Uses	Membrane key switch Aircraft applications Insulating material Connector Communication Equipment
Agency Ratings	MIL C-24308
Forms	flake
Processing Method	Resin transfer molding Compression molding Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.79	g/cm³	ASTM D792
Bulk Factor	6.0		ASTM D1895
Molding Shrinkage - Flow (Compression Molded)	0.15 - 0.35	%	ASTM D955

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength	68.9	MPa	ASTM D638
Flexural Modulus	13800	MPa	ASTM D790
Flexural Strength	131	MPa	ASTM D790
Compressive Strength	152	MPa	ASTM D695

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	190	J/m	ASTM D256A

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	260	°C	ASTM D648
CLTE - Flow	2.2E-5	cm/cm/°C	ASTM D696
Thermal Conductivity	0.31	W/m/K	ASTM C177

Electrical	Nominal Value	Unit	Test Method
Dielectric Strength			ASTM D149
-- ¹	15	kV/mm	ASTM D149
-- ²	14	kV/mm	ASTM D149
Dielectric Constant			ASTM D150
1 kHz	4.50		ASTM D150
1 MHz	4.30		ASTM D150
Dissipation Factor			ASTM D150
1 kHz	0.010		ASTM D150
1 MHz	0.016		ASTM D150
Arc Resistance	133	sec	ASTM D495
Comparative Tracking Index (CTI)	600	V	UL 746

Flammability	Nominal Value	Unit	Test Method
Oxygen Index	30	%	ASTM D2863

Injection	Nominal Value	Unit
Rear Temperature	60.0	°C
Middle Temperature	76.7	°C
Nozzle Temperature	87.8	°C
Processing (Melt) Temp	110 - 116	°C
Mold Temperature	160 - 182	°C

Injection instructions
Plastication: 50rpmBack Pressure (gauge): slightInjection Pressure: set to give 5 to 15 sec injection timeHold Pressure: 1/2 of injection pressureCure Time, 0.125 in: 40 secThe value listed as Thermal Conductivity, ASTM C177, was tested in accordance with ASTM F433.Resin Isomer, DAP: OrthoWater Absorption, ASTM D570, 48 hrs, 50°C: 0.32%Flammability Ignition, ASTM D229: 90 secFlammability Burn, ASTM D229: 60 secDielectric Strength, ASTM D149, 60 Hz, Method A, wet: 375 V/milDielectric Strength, ASTM D149, 60 Hz, Method B, wet: 350 V/milDielectric Constant, ASTM D150, 1000 Hz, wet: 4.5Dielectric Constant, ASTM D150, 1000000 Hz, wet: 4.3Dissipation Factor, ASTM D150, 1000 Hz, wet: 0.01Dissipation Factor, ASTM D150, 1000000 Hz, wet: 0.016Compression and Transfer Molding Conditions: Preforming Pressure: 8000 to 12000 psi Preheat Temperature: 220 to 230 °F Preheat Time: 45 sec Mold Temperature: 320 to 350 °F Compression Mold Pressure: 3500 to 6000 psi Transfer Mold Pressure: 2500 to 5000 psi Cure Time, 0.125 in: 45 to 70 sec

Injection instructions

Plastication: 50rpmBack Pressure (gauge): slightInjection Pressure: set to give 5 to 15 sec injection timeHold Pressure: 1/2 of injection pressureCure Time, 0.125 in: 40 secThe value listed as Thermal Conductivity, ASTM C177, was tested in accordance with ASTM F433.Resin Isomer, DAP: OrthoWater Absorption, ASTM D570, 48 hrs, 50°C: 0.32%Flammability Ignition, ASTM D229: 90 secFlammability Burn, ASTM D229: 60 secDielectric Strength, ASTM D149, 60 Hz, Method A, wet: 375 V/milDielectric Strength, ASTM D149, 60 Hz, Method B, wet: 350 V/milDielectric Constant, ASTM D150, 1000 Hz, wet: 4.5Dielectric Constant, ASTM D150, 1000000 Hz, wet: 4.3Dissipation Factor, ASTM D150, 1000 Hz, wet: 0.01Dissipation Factor, ASTM D150, 1000000 Hz, wet: 0.016Compression and Transfer Molding Conditions: Preforming Pressure: 8000 to 12000 psi Preheat Temperature: 220 to 230 °F Preheat Time: 45 sec Mold Temperature: 320 to 350 °F Compression Mold Pressure: 3500 to 6000 psi Transfer Mold Pressure: 2500 to 5000 psi Cure Time, 0.125 in: 45 to 70 sec

Note Message
1 .	Method A (short time)
2 .	Method B (step by step)

Category:	DAP , Diallyl Phthalate
Manufacturer:	Vyncolit N.V.
Trademark:	Vyncolit®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	swbKlK_Vyncolit-52-40-40.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Sylvin 8225-65 Orange 580	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
MonoSol® M1040	MonoSol, LLC	PVOH	MonoSol®
Aristech S-300	Aristech Acrylics LLC	Acrylic, Unspecified	Aristech
Hostacom G3 R05 105555	LyondellBasell Industries	PP Homopolymer	Hostacom
MAJORIS GT 275	AD majoris	PP, Unspecified	MAJORIS