Bio-Flex® F 1130
| Category: | PLA , Polylactic Acid |
| Manufacturer: | FKuR Kunststoff GmbH |
| Trademark: | Bio-Flex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | swIrkd_Bio-Flex-F-1130.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Biodegradable compound for film extrusion Bio-Flex® F 1130 (prev. Bio-Flex® 219F) |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Apparent Density | 0.83 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 - 5.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 1.50 - 4.00 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 390 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 17.0 | MPa | ISO 527-2 |
| Flexural Modulus | 370 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 9.00 | MPa | ISO 178 |
| Tensile Strain at Tensile Strength | > 300 | % | ISO 527 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Permeability (45.0 µm) | 850 | cm³/m²/bar/24 hr | ISO 15105-2 |
| Nitrogen Permeability (45.0 µm) | 160 | cm³/m²/bar/24 hr | DIN 53380-2 |
| Water Vapor Transmission Rate (45 µm) | 70 | g/m²/24 hr | ISO 15106-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (24°C) | No Break | ISO 179/1eA | |
| Charpy Unnotched Impact Strength (24°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 89.0 | °C | ISO 306/A |
| Melting Temperature (DSC) | > 155 | °C | ISO 3146 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.30 | % | |
| Cylinder Zone 1 Temp. | 160 | °C | |
| Cylinder Zone 2 Temp. | 160 | °C | |
| Cylinder Zone 3 Temp. | 165 | °C | |
| Cylinder Zone 4 Temp. | 170 | °C | |
| Adapter Temperature | 170 | °C | |
| Melt Temperature | < 190 | °C | |
| Die Temperature | 175 | °C |
| Extrusion instructions |
|---|
| Water jacket (feed): 35 [°C]Die gap: 0.8 - 1.4 mmDie diameter: up to 400 mmBlow film ratio: 2.5 - 4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| StarMediflex P 7060-1000 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | StarMediflex |
| Sylvin 2910-60 Blue 8389 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| VINIKA® CE55EG | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| HIPOLEN P® TA 41G | Hipol a.d. | PP Homopolymer | HIPOLEN P® |
| Sinpolene CPP5540 | Teknor Apex Asia Pacific PTE. LTD. | PP, Unspecified | SINPOLENE |