MARCOBLEND MB101
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | POLY GIN |
| Trademark: | MARCOBLEND |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | svnfm7_MARCOBLEND-MB101.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MARCOBLEND MB101 is glass fiber 15% reinforced ABS resin. The resin is The unique characters include superior processability, good stiffness, and excellent dimension stability and suitable for use in TV back cover and internal structure parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (240°C/5.0 kg) | 28 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 to 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 54.0 | MPa | ASTM D638 |
| Flexural Modulus | 2820 | MPa | ASTM D790 |
| Flexural Strength | 81.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 76 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 88.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 230 to 245 | °C | |
| Middle Temperature | 240 to 255 | °C | |
| Front Temperature | 245 to 255 | °C | |
| Nozzle Temperature | 240 to 250 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAYPRENE® NB221-S4042 | R&P (Pte.) Ltd. | TPE | RAYPRENE® |
| Skyrol® SH64 | SKC Inc. | PET | Skyrol® |
| ACCUCOMP™ ABS801L | ACLO Compounders Inc. | ABS | ACCUCOMP™ |
| ELASTOSIL® R plus 4001/70 | Wacker Chemie AG | Silicone | ELASTOSIL® R plus |
| Hifax M2 U13 | LyondellBasell Industries | PP Homopolymer | Hifax |